熱応答性およびpH応答性スイッチング挙動を有するポリスルフォンと二元側鎖を有するグラフト共重合体とのブレンドから調製したロバストな刺激応答膜

Robust Stimuli-Responsive Membranes Prepared from a Blend of Polysulfone and a Graft Copolymer Bearing Binary Side Chains with Thermo- and pH-Responsive Switching Behavior

著者 (24件)： Miao Lei (Foshan University, Jiangwan 1st Road 18, 528000, Foshan, P. R. China) ,  Miao Lei (Guangzhou Institute of Chemistry, Chinese Academy of Sciences, Xingke Road 368, 510675, Guangzhou, P. R. China) ,  Miao Lei (Key Laboratory of Cellulose and Lignocellulosics Chemistry, Chinese Academy of Sciences, 510650, Guangzhou, P. R. China) ,  Miao Lei (Guangdong Provincial Key Laboratory of Organic Polymer Materials for Electronics, 510650, Guangzhou, P. R. China) ,  Tu Yuanyuan (Guangzhou Institute of Chemistry, Chinese Academy of Sciences, Xingke Road 368, 510675, Guangzhou, P. R. China) ,  Tu Yuanyuan (Key Laboratory of Cellulose and Lignocellulosics Chemistry, Chinese Academy of Sciences, 510650, Guangzhou, P. R. China) ,  Tu Yuanyuan (Guangdong Provincial Key Laboratory of Organic Polymer Materials for Electronics, 510650, Guangzhou, P. R. China) ,  Yang Yang (Guangzhou Institute of Chemistry, Chinese Academy of Sciences, Xingke Road 368, 510675, Guangzhou, P. R. China) ,  Yang Yang (Key Laboratory of Cellulose and Lignocellulosics Chemistry, Chinese Academy of Sciences, 510650, Guangzhou, P. R. China) ,  Yang Yang (Guangdong Provincial Key Laboratory of Organic Polymer Materials for Electronics, 510650, Guangzhou, P. R. China) ,  Lin Shudong (Guangzhou Institute of Chemistry, Chinese Academy of Sciences, Xingke Road 368, 510675, Guangzhou, P. R. China) ,  Lin Shudong (Key Laboratory of Cellulose and Lignocellulosics Chemistry, Chinese Academy of Sciences, 510650, Guangzhou, P. R. China) ,  Lin Shudong (Guangdong Provincial Key Laboratory of Organic Polymer Materials for Electronics, 510650, Guangzhou, P. R. China) ,  Hu Jiwen (Guangzhou Institute of Chemistry, Chinese Academy of Sciences, Xingke Road 368, 510675, Guangzhou, P. R. China) ,  Hu Jiwen (Key Laboratory of Cellulose and Lignocellulosics Chemistry, Chinese Academy of Sciences, 510650, Guangzhou, P. R. China) ,  Hu Jiwen (Guangdong Provincial Key Laboratory of Organic Polymer Materials for Electronics, 510650, Guangzhou, P. R. China) ,  Zhang Min (Foshan University, Jiangwan 1st Road 18, 528000, Foshan, P. R. China) ,  Li Yue (Foshan University, Jiangwan 1st Road 18, 528000, Foshan, P. R. China) ,  Li Fei (Guangzhou Institute of Chemistry, Chinese Academy of Sciences, Xingke Road 368, 510675, Guangzhou, P. R. China) ,  Li Fei (Key Laboratory of Cellulose and Lignocellulosics Chemistry, Chinese Academy of Sciences, 510650, Guangzhou, P. R. China) ,  Li Fei (Guangdong Provincial Key Laboratory of Organic Polymer Materials for Electronics, 510650, Guangzhou, P. R. China) ,  Mo Yangmiao (Guangzhou Institute of Chemistry, Chinese Academy of Sciences, Xingke Road 368, 510675, Guangzhou, P. R. China) ,  Mo Yangmiao (Key Laboratory of Cellulose and Lignocellulosics Chemistry, Chinese Academy of Sciences, 510650, Guangzhou, P. R. China) ,  Mo Yangmiao (Guangdong Provincial Key Laboratory of Organic Polymer Materials for Electronics, 510650, Guangzhou, P. R. China)
資料名： Chemistry - European Journal  (Chemistry - European Journal)
巻： 23  号： 32  ページ： 7737-7747  発行年： 2017年 
JST資料番号： W0744A  ISSN： 0947-6539  CODEN： CEUJED  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 独立なpH応答挙動および温度応答挙動を示す刺激応答膜を,機能性両親媒性二元グラフト共重合体,つまり,ポリスルホン-グラフト-(ポリ(イソプロピルアクリルアミド-co-アクリル酸)-ランダム-ポリ(メチルアクリラート))(PSf-g-(P(NIPAAm-co-AA)-r-PMMA)と表示)と市販のポリスルホンとの混合から製造した。P(NIPAAm-co-AA)側鎖の長さが異なる2種類のグラフト共重合体を設計し,膜表面で濃縮して,熱応答性およびpH応答性オンオフ スイッチとして使用した。これら2種類のポリマブレンド膜の二重応答挙動間の相違を,水フラックス測定および接触角測定によって調べた。PMMA側鎖は,グラフト共重合体に関する膜基板への確実な固定に役立ち,二元グラフト共重合体から調製した混合膜は,単一グラフト共重合体PSf-g-P(NIPAAm-co-AA)から調製した膜よりも安定であり,よりロバストな刺激応答を示した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ポリスルホン ,  *グラフト共重合体 ,  *混合物 ,  両親媒性 ,  熱応答 ,  pH依存性 ,  *刺激応答性高分子 ,  *高分子膜 ,  ポリマブレンド ,  側鎖 ,  鎖長効果 ,  接触角 ,  物質流束 ,  ポリメタクリル酸メチル ,  不飽和脂肪酸 ,  ビニル化合物 ,  カルボン酸エステル ,  脂肪族カルボン酸 ,  不飽和カルボン酸
準シソーラス用語： pH応答性 ,  水フラックス

著者キーワード (5件)： copolymerization ,  filtration ,  membranes ,  polymers ,  stimuli-responsive materials

分類 (1件)： 高分子固体の物理的性質  (CG02024U)

物質索引 (3件)： アクリル酸メチル ,  アクリル酸 ,  N-イソプロピルアクリルアミド

タイトルに関連する用語 (11件)： 熱応答性 ,  pH応答性 ,  スイッチング ,  挙動 ,  ポリスルフォン ,  側鎖 ,  グラフト共重合体 ,  ブレンド ,  調製 ,  ロバスト ,  刺激応答