化学的に還元されたグラフェンエアロゲルの電磁干渉遮蔽特性と機構【Powered by NICT】

Electromagnetic interference shielding properties and mechanisms of chemically reduced graphene aerogels

著者 (6件)： Bi Shuguang (Temasek Laboratories, Nanyang Technological University, 50 Nanyang Drive, 637553, Singapore) ,  Zhang Liying (Temasek Laboratories, Nanyang Technological University, 50 Nanyang Drive, 637553, Singapore) ,  Mu Chenzhong (School of Material Science and Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798, Singapore) ,  Liu Ming (Temasek Laboratories, Nanyang Technological University, 50 Nanyang Drive, 637553, Singapore) ,  Hu Xiao (Temasek Laboratories, Nanyang Technological University, 50 Nanyang Drive, 637553, Singapore) ,  Hu Xiao (School of Material Science and Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798, Singapore)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 412  ページ： 529-536  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： グラフェンは優れた電磁干渉(EMI)遮蔽性能を示すことを実証した。本研究では,超軽量(~5.5mg/cm~3)グラフェンエアロゲル(GA)は,凍結乾燥とそれに続く化学還元法を用いて酸化グラフェン(GO)の組織化により作製した。GAのEMI遮蔽特性と機構は,還元グラフェン酸化物(rGO)シートと特異な多孔質ネットワークの固有特性に関して系統的に研究した。GOは高濃度のヒドラジン蒸気の減少した場合GAのEMI遮蔽有効性(SE)は20.4~27.6dB増加した。より多くの窒素原子から.~二つのグラファイト格子および自由電子の存在は,強化されたEMI SEの結果を与えた。吸収はGAの支配的な遮蔽機構であった。コンパクト薄膜への高多孔性GAの圧縮EMI SEを変化させなかったが,反射吸収からの主要な遮蔽機構をシフトした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ネットワーク ,  グラファイト ,  凍結乾燥 ,  *電磁干渉 ,  ヒドラジン ,  *グラフェン ,  薄膜 ,  多孔性
準シソーラス用語： 自由電子 ,  窒素原子 ,  高濃度 ,  酸化グラフェン ,  軽量 , 【Automatic Indexing@JST】

著者キーワード (3件)： 化学的還元 ,  グラフェンエアロゲル ,  EMI遮蔽機構