新しい疎水性ポリフェノール橋かけ剤と共重合した熱応答性N イソプロピルアクリルアミドヒドロゲルの合成と特性化【Powered by NICT】

Synthesis and characterization of thermally responsive N-isopropylacrylamide hydrogels copolymerized with novel hydrophobic polyphenolic crosslinkers

著者 (6件)： Tang Shuo (Department of Chemical and Materials Engineering, University of Kentucky, Lexington, KY 40506, USA) ,  Bhandari Rohit (Department of Chemical and Materials Engineering, University of Kentucky, Lexington, KY 40506, USA) ,  Delaney Sean P. (Department of Pharmaceutical Sciences, University of Kentucky, Lexington, KY 40506, USA) ,  Munson Eric J. (Department of Pharmaceutical Sciences, University of Kentucky, Lexington, KY 40506, USA) ,  Dziubla Thomas D. (Department of Chemical and Materials Engineering, University of Kentucky, Lexington, KY 40506, USA) ,  Hilt J. Zach (Department of Chemical and Materials Engineering, University of Kentucky, Lexington, KY 40506, USA)
資料名： Materials Today Communications  (Materials Today Communications)
巻： 10  ページ： 46-53  発行年： 2017年 
JST資料番号： W3060A  ISSN： 2352-4928  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 二系列の熱感受性ヒドロゲルを種々の含有量新規疎水性架橋剤,クルクミン光(CMA)及びケルセチン光(QMA)のN イソプロピルアクリルアミド(NIPAAm)の共重合により合成した。得られたヒドロゲルの組成は固体NMR(ss NMR)を用いて特性化し,温度依存膨潤挙動と下限臨界溶解温度(LCST)を膨潤研究と示差走査熱量測定(DSC)を用いて特性化した。架橋剤含有量の増加によって,ヒドロゲルのLCSTと膨潤比の有意な減少,CMAまたはQMAにより導入された疎水性の増加に帰することができた。全てのヒドロゲルのは架橋剤含有量と共に膨潤減少の程度と温度応答性膨潤を示した。低架橋剤含有量ゲルは鋭い相転移を示したが,高い架橋剤含有量のゲルはより広い相転移を有していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 示差走査熱量測定 ,  *熱応答 ,  温度依存性 ,  *疎水性 ,  *ゲル ,  *キャラクタリゼーション ,  膨潤 ,  *多価フェノール ,  相転移 ,  感受性 ,  *共重合 ,  *ヒドロゲル
準シソーラス用語： LCST , 【Automatic Indexing@JST】

分類 (1件)： 共重合  (CG04030D)

タイトルに関連する用語 (6件)： 疎水性 ,  ポリフェノール ,  橋かけ剤 ,  共重合 ,  熱応答性 ,  特性化