超音波付加製造により作製した6061アルミニウム合金に及ぼす溶接後熱処理の影響【Powered by NICT】

Effect of post weld heat treatment on the 6061 aluminum alloy produced by ultrasonic additive manufacturing

著者 (7件)： Gussev M.N. (Oak Ridge National Laboratory, Oak Ridge, TN 37831, United States) ,  Sridharan N. (Oak Ridge National Laboratory, Oak Ridge, TN 37831, United States) ,  Sridharan N. (University of Tennessee, Knoxville, TN 37916, United States) ,  Norfolk M. (Fabrisonic LLC, Columbus, OH 43221, United States) ,  Terrani K.A. (Oak Ridge National Laboratory, Oak Ridge, TN 37831, United States) ,  Babu S.S. (Oak Ridge National Laboratory, Oak Ridge, TN 37831, United States) ,  Babu S.S. (University of Tennessee, Knoxville, TN 37916, United States)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 684  ページ： 606-616  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 超音波付加製造(UAM)は,完全に機能的な部品を作製するために機械化されたテープ層と結合した超音波溶接の原理を用いた固体状態の付加的製造技術である。しかし,溶接界面(Z方向)に垂直に負荷された場合UAMを用いて作製した部品は,しばしば強度レベルの低下を示した。本研究では,UAMプロセスを用いて作製したAl-6061ビルドに及ぼす溶接後熱処理(PWHT)の影響を,UAMビルドの機械的強度を向上させることを目的として検討した。金属組織学と共にマルチスケール構造特性化(SEM EBSD)と結合したディジタル画像相関(DIC)を引張試験では,UAMビルドの機械的性能を検討し,合理的に説明するために使用した。PWHTは約3~3.5倍(~46 177MPa)ゼット強度レベルを改善する可能性があることを確認した。強度レベルの改良は主に,結合界面を横切る材料時効と粒成長により実施した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 生産技術 ,  金属組織学 ,  引張試験 ,  *溶接 ,  構造特性 ,  超音波溶接 ,  界面 ,  *超音波 ,  *熱処理 ,  固相 ,  機械的強度 ,  *アルミニウム合金
準シソーラス用語： 機械的性能 ,  ディジタル画像相関 ,  マルチスケール , 【Automatic Indexing@JST】

著者キーワード (5件)： 超音波添加剤は製造 ,  後は溶接熱処理 ,  電子後方散乱回折 ,  ディジタル画像相関 ,  引張試験

分類 (2件)： 溶接部  (WC07100I) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 超音波 ,  付加製造 ,  作製 ,  アルミニウム合金 ,  溶接後熱処理