ナノインデンテーションにより研究した安定化ジルコニアセラミックの歪に誘起された相変態挙動【Powered by NICT】

Strain-induced phase transformation behavior of stabilized zirconia ceramics studied via nanoindentation

著者 (6件)： Liu Erqiang (College of Applied Science, Taiyuan University of Science and Technology, Taiyuan 030024, China) ,  Xiao Gesheng (Institute of Applied Mechanics and Biomedical Engineering, Taiyuan University of Technology, Taiyuan 030024, China) ,  Jia Wufei (Institute of Applied Mechanics and Biomedical Engineering, Taiyuan University of Technology, Taiyuan 030024, China) ,  Shu Xuefeng (Institute of Applied Mechanics and Biomedical Engineering, Taiyuan University of Technology, Taiyuan 030024, China) ,  Yang Xuexia (College of Applied Science, Taiyuan University of Science and Technology, Taiyuan 030024, China) ,  Wang Yulei (College of Applied Science, Taiyuan University of Science and Technology, Taiyuan 030024, China)
資料名： Journal of the Mechanical Behavior of Biomedical Materials  (Journal of the Mechanical Behavior of Biomedical Materials)
巻： 75  ページ： 14-19  発行年： 2017年 
JST資料番号： W2351A  ISSN： 1751-6161  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 異なる歪速度と押込み深さで正方晶-単斜晶(T M)相変態挙動を研究するために,連続剛性測定で安定化したジルコニアセラミックスについて行ったナノインデンテーション試験。結果は低および高歪速度で減少した相変態速度を示したが,負荷中の中程度の歪速度下で速度を増加させた。相変態プロセスはP/Pに敏感であったが,最終的な体積分率はほとんど同一(45%)。さらに,相変態の大部分は短い初期時間保持時間とM期体積分率のわずかな線形増加が続いで完了した。定ひずみ速度で押込まれた相変態は,インデンテーション深さの増加と共に低下した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 歪速度 ,  剛性 ,  *ナノインデンテーション ,  線形性 ,  正方晶系 ,  体積率 ,  *セラミック ,  単斜晶系 ,  保持時間
準シソーラス用語： 高ひずみ速度 ,  押込み深さ ,  *ジルコニアセラミック , 【Automatic Indexing@JST】

著者キーワード (4件)： 安定化ジルコニアセラミック ,  連続剛性測定 ,  ナノインデンテーション ,  正方晶-単斜晶相変態挙動

分類 (2件)： 歯科材料  (GT06000B) ,  医用素材  (GA05040H)

タイトルに関連する用語 (7件)： ナノインデンテーション ,  研究 ,  安定化 ,  ジルコニアセラミック ,  誘起 ,  相変態 ,  挙動