Ir_3X金属間化合物の弾性異方性と機械的強度のモデル化【Powered by NICT】

Modeling the elastic anisotropies and mechanical strengths of Ir₃X intermetallics

著者 (5件)： Yan Haiyan (College of Chemistry and Chemical Engineering, Baoji University of Arts and Sciences, Baoji 721013, China) ,  Zhang Meiguang (College of Physics and Optoelectronic Technology, Nonlinear Research Institute, Baoji University of Arts and Sciences, Baoji 721016, China) ,  Zheng Baobing (College of Physics and Optoelectronic Technology, Nonlinear Research Institute, Baoji University of Arts and Sciences, Baoji 721016, China) ,  Wei Qun (School of Physics and Optoelectronic Engineering, Xidian University, Xi’an 710071, China) ,  Zhang Yun (College of Physics and Optoelectronic Technology, Nonlinear Research Institute, Baoji University of Arts and Sciences, Baoji 721016, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 696  ページ： 611-618  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： fcc Ir金属と比較してL1_2金属間化合物Ir_3X(X=V,Nb,Ta)の弾性異方性と機械的強度を,第一原理計算を用いて研究した。弾性異方性計算はIr_3Taは他の二Ir_3X金属間化合物とfcc Irと比較してYoung率,Poisson比,剪断係数,それぞれ,最大の異方性を示すことが分かった。三Ir_3X金属間化合物の計算された理想的な引張強さおよび臨界引張歪はfcc Irのそれらよりも大きく,L1_2Ir_3X相は機械的に硬く,脆さの少ないことを示した。L1_2Ir_3Xの大きな歪での理想的なせん断強度を調べ,得られた結果は,Ir_3X相の格子不安定性はIrX結合の破れと格子再構成を通した新しい斜方晶構造の形成を伴う(111)<1 10>方向で起こることを示唆した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 脆性 ,  Young率 ,  斜方晶系 ,  引張強さ ,  *機械的強度 ,  剪断強さ ,  Poisson比 ,  *モデリング ,  剪断係数 ,  *金属間化合物 ,  再構成 ,  *異方性
準シソーラス用語： 引張歪 ,  第一原理計算 ,  *弾性異方性 , 【Automatic Indexing@JST】

著者キーワード (4件)： 第一原理計算 ,  金属間化合物 ,  弾性異方性 ,  機械的強度