複合膜の特性に対するPVA/澱粉の架橋と修正されたオオムギ籾殻の強化の影響【Powered by NICT】

Effect of cross linking of PVA/starch and reinforcement of modified barley husk on the properties of composite films

著者 (6件)： Mittal Aanchal (Department of Chemical Engineering, National Institute of Technology, Jalandhar 144 011, Punjab, India) ,  Garg Sangeeta (Department of Chemical Engineering, National Institute of Technology, Jalandhar 144 011, Punjab, India) ,  Kohli Deepak (Department of Chemical Engineering, National Institute of Technology, Jalandhar 144 011, Punjab, India) ,  Maiti Mithu (Department of Chemistry, National Institute of Technology, Jalandhar 144 011, Punjab, India) ,  Jana Asim Kumar (Department of Biotechnology, National Institute of Technology, Jalandhar 144 011, Punjab, India) ,  Bajpai Shailendra (Department of Chemical Engineering, National Institute of Technology, Jalandhar 144 011, Punjab, India)
資料名： Carbohydrate Polymers  (Carbohydrate Polymers)
巻： 151  ページ： 926-938  発行年： 2016年 
JST資料番号： E0961A  ISSN： 0144-8617  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： オオムギ殻(BH)したパルミチン酸によるグラフト共重合した。BHの結晶挙動は,グラフト化後に減少した。ポリビニルアルコール(PVA)/澱粉(St)ブレンド膜,尿素ホルムアルデヒド架橋PVA/St膜と天然BH,グラフトされたBHを含む複合膜を別々に調製した。尿素/澱粉比,機械的性質に及ぼすBHとグラフト化BHの含有量,吸水(%),および複合膜の生分解性の効果が観察された。ブレンド中の尿素:澱粉比0から0.5への増加に伴い,架橋フィルムの引張強さはPVA/St膜と比較して40.23%増加した。しかし,グラフトされたBH複合膜の,引張強さはPVA/St膜よりも72.4%増加した。天然BH複合膜の分解速度はPVA/St膜よりも速かった。種々の膜をSEM,FT-IRおよび熱分析によって特性化した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 微生物分解性 ,  *オオムギ ,  キャラクタリゼーション ,  移植片 ,  引張強さ ,  機械的性質 ,  グラフト共重合 ,  吸水 ,  *複合膜 ,  熱分析 ,  結晶 ,  脂肪酸
準シソーラス用語： 分解速度 , 【Automatic Indexing@JST】

著者キーワード (6件)： PVA/St膜 ,  架橋膜 ,  オオムギ殻 ,  パルミチン酸グラフト化 ,  複合膜 ,  機械的性質

分類 (2件)： 高分子固体のその他の性質  (CG02025L) ,  多糖類  (CF10054P)

物質索引 (1件)： パルミチン酸

タイトルに関連する用語 (6件)： 複合膜 ,  澱粉 ,  架橋 ,  オオムギ ,  籾殻 ,  強化