NaCl-KCl-CsCl溶融塩からのIr被覆析出の電気化学的研究【Powered by NICT】

Electrochemical studies of Ir coating deposition from NaCl-KCl-CsCl molten salts

著者 (5件)： Huang Yongle (College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073, PR China) ,  Bai Shuxin (College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073, PR China) ,  Zhang Hong (College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073, PR China) ,  Ye Yicong (College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073, PR China) ,  Zhu Li’’an (College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073, PR China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 322  ページ： 76-85  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本論文では,融解NaCl KCl CsCl IrCl_3と主な速度論的パラメータにおけるIr~3+イオンの電気化学的挙動を823Kから913Kまでの過渡および定常電気化学的方法により調べた。Ir皮膜の微細構造に及ぼすIr~3+イオンの電気化学の影響についても考察した。融液からIr~3+イオンの電気化学的還元した,823K883Kで三電子の交換を伴う拡散律速と不可逆反応と準可逆であるに変換温度913Kまで増加した。Ir~3+/Ir対,拡散係数D_0と交換電流密度j_0の主要な動力学的パラメータは温度と共に2.4×10~ 6cm~2/sから9.2×10~ 6cm~2/sと5mA/cm~2から16mA/cm~2に増加した。温度と印加カソード電位減少とともに,Ir被覆の微細構造は粗と優先配向した柱状結晶粒構造から微細で非配向分散結晶粒構造に変化した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 優先配向 ,  カソード還元 ,  *被覆 ,  皮膜 ,  *塩化ナトリウム ,  拡散律速 ,  *電気化学 ,  微細構造 ,  *融解塩 ,  結晶粒 ,  不可逆反応 ,  速度論 ,  *イリジウム ,  拡散係数 ,  電気化学的挙動

著者キーワード (6件)： 電気化学 ,  Microstructure ,  イリジウム ,  融液 ,  クロノポテンシオメトリー ,  電気化学的インピーダンススペクトル

分類 (4件)： 金属材料へのセラミック被覆  (YC02050V) ,  炭素とその化合物  (YB02060D) ,  拡散浸透めっき  (WC08025J) ,  防食  (WB03040M)

タイトルに関連する用語 (7件)： NaCl ,  CsCl ,  溶融塩 ,  Ir ,  析出 ,  電気化学 ,  研究