NbドーピングによるNa_2Ti_3O_7のsodiation性能の改善【Powered by NICT】

Improving the sodiation performance of Na₂Ti₃O₇ through Nb-doping

著者 (6件)： Chen Jizhang (College of Materials Science and Engineering, Nanjing Forestry University, Nanjing 210037, China) ,  Zhou Xiaoyan (College of Materials Science and Engineering, Nanjing Forestry University, Nanjing 210037, China) ,  Mei Changtong (College of Materials Science and Engineering, Nanjing Forestry University, Nanjing 210037, China) ,  Xu Junling (Department of Electronic Engineering, The Chinese University of Hong Kong, New Territories, Hong Kong) ,  Wong Ching-Ping (Department of Electronic Engineering, The Chinese University of Hong Kong, New Territories, Hong Kong) ,  Wong Ching-Ping (School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA 30332, United States)
資料名： Electrochimica Acta  (Electrochimica Acta)
巻： 224  ページ： 446-451  発行年： 2017年 
JST資料番号： B0535B  ISSN： 0013-4686  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Na_2Ti_3O_7はNaイオン電池用の有望なアノード材料として注目を集めている。Na_2Ti_3O_7の低い電子伝導率は,ナトリウムの約動力学問題をもたらす。本研究では,簡易なゾル-ゲル法から合成したNbドープNa_2Ti_3O_7を報告した。得られたNa_2Ti_2 0.97Nb_0 0.03O_7は元のNa_2Ti_3O_7と比較して単位胞体積及び低下したバンドギャップを増加させた。Na_2Ti_2 0.97Nb_0 0.03O_7は0.2で189.7mAhg~( 1)C,5Cで89.4mAhg~( 1)の非常に高レート性能及び500サイクル後に78.5%の大きなサイクル性の高い可逆容量を示した。特に,Na_2Ti_2 0.97Nb_0 0.03O_7のレート能力は元Na_2Ti_3O_7のそれに比べ著しく優れている。改良ナトリウム性能はNbドーピングはNa_2Ti_3O_7アノード材料のための効果的な改質であることを示唆する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *ドーピング ,  バンドギャップ ,  電池容量 ,  *ニオブ ,  アノード ,  ゾル-ゲル法 ,  ナトリウム
準シソーラス用語： 可逆容量 ,  単位格子 ,  電子伝導率 ,  アノード材料【電池】 ,  ナトリウムイオン蓄電池 , 【Automatic Indexing@JST】

著者キーワード (5件)： Naイオン電池 ,  アノード ,  Na_2Ti_3O_7 ,  sodiation ,  Nbドーピング

分類 (1件)： 二次電池  (YB04030K)

タイトルに関連する用語 (2件)： Nb ,  ドーピング