5754Al合金の摩耗挙動に及ぼす陰極水素チャージの影響【Powered by NICT】

Effect of cathodic hydrogen charging on the wear behavior of 5754 Al alloy

著者 (9件)： Georgiou E.P. (K.U.Leuven, Dept. Materials Engineering (MTM), Kasteelpark Arenberg 44, B-3001 Leuven, Belgium) ,  Georgiou E.P. (Falex Tribology N.V., Wingepark 23B, B3110 Rotselaar, Belgium) ,  Cevallos V.P. (K.U.Leuven, Dept. Materials Engineering (MTM), Kasteelpark Arenberg 44, B-3001 Leuven, Belgium) ,  Van der Donck T. (K.U.Leuven, Dept. Materials Engineering (MTM), Kasteelpark Arenberg 44, B-3001 Leuven, Belgium) ,  Drees D. (Falex Tribology N.V., Wingepark 23B, B3110 Rotselaar, Belgium) ,  Meersschaut J. (IMEC, Kapeldreef 75, Leuven 3001, Belgium) ,  Panagopoulos C.N. (Laboratory of Physical Metallurgy, National Technical University of Athens, Zografos, 15780 Athens, Greece) ,  Celis J.-P. (K.U.Leuven, Dept. Materials Engineering (MTM), Kasteelpark Arenberg 44, B-3001 Leuven, Belgium) ,  Celis J.-P. (Falex Tribology N.V., Wingepark 23B, B3110 Rotselaar, Belgium)
資料名： Wear  (Wear)
巻： 390-391  ページ： 295-301  発行年： 2017年 
JST資料番号： E0377A  ISSN： 0043-1648  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究は,5754Al合金の構造とトライボロジー特性に及ぼす水素吸収の影響を研究することに焦点を当てた。目的は,水素取込と摩耗の間の相乗作用を理解することである。特に,水素は,3MのHCl水溶液中での定電流分極による表面に導入した。合金の表面層へと選ばれた充電条件のための水素の取り込みは,ブリスタリングをもたらした。アルミニウム水素化物は水素チャージした試料のX線回折で検出されなかったが,表面層中の水素含有量を弾性反跳検出分析によって定量化した。水素取込後の表面層の硬化が観察された。アルミナ相手材として合金の滑り摩耗抵抗はかなり変化し,水素チャージ条件,水素チャージと摩擦の間の相乗効果,接触界面でのトライボ層の形成に依存することが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 滑り摩耗 ,  充電 ,  相乗作用 ,  X線回折 ,  水素吸蔵 ,  ブリスタリング ,  塩酸 ,  *水素 ,  アルミニウム合金 ,  アルミニウム ,  水溶液 ,  アルミナ ,  表層 ,  水素化物
準シソーラス用語： *水素チャージ , 【Automatic Indexing@JST】

著者キーワード (5件)： アルミニウム合金 ,  水素脆化 ,  滑り摩耗 ,  水素帯電 ,  表面特性

分類 (2件)： 潤滑一般  (QB02010S) ,  金属の機械的性質  (BL01022T)

タイトルに関連する用語 (3件)： 摩耗挙動 ,  陰極 ,  水素チャージ