316Lオーステナイト系ステンレス鋼の引張試験中の双晶境界の発達と亀裂発生挙動に及ぼすその場観察【Powered by NICT】

In-situ observation on twin boundary evolution and crack initiation behavior during tensile test on 316L austenitic stainless steel

著者 (5件)： Wang Wei (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Liu Tingguang (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Cao Xinyuan (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Lu Yonghao (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Shoji Tetsuo (Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579, Japan)
資料名： Materials Characterization  (Materials Characterization)
巻： 132  ページ： 169-174  発行年： 2017年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本論文では,電子後方散乱回折(EBSD)法による316Lステンレス鋼の引張試験中の双晶境界の発達と亀裂発生挙動に及ぼすその場観察を報告した。結果は明確な伸長後の双晶境界で開始された双晶境界伸長増加と亀裂につれて次第に減少の割合であることを示した。双晶境界に加えて二結晶粒間のシュミット因子値の差は伸びの増加,これは双晶境界に結晶粒内の転位の動きを連続的に増加した。高密度の転位が双晶境界の二面,双晶境界は,引張中に歪を蓄積することを示した間の大きな局部誤配向値の差をもたらした。その結果,双晶がオーステナイト結晶粒とのコインシデンスサイト格子を失い,双晶境界はランダム高角度に変換し,双晶境界は形質転換したが最終的には高傾角粒界での亀裂の開始をもたらした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *引張試験 ,  *双晶 ,  *双晶境界 ,  *オーステナイト ,  *亀裂 ,  *オーステナイト系ステンレス鋼 ,  *引張 ,  *亀裂発生 ,  コインシデンス格子 ,  結晶粒 ,  *その場観察 ,  高傾角粒界
準シソーラス用語： ミスオリエンテーション ,  EBSD ,  *SUS316L , 【Automatic Indexing@JST】

著者キーワード (5件)： 双晶境界 ,  電子後方散乱回折 ,  すべり系 ,  その場引張試験 ,  Schmid因子