多孔質Si_3N_4セラミックに及ぼすβSi_3N_4ベース環境障壁コーティングの作製と熱衝撃抵抗【Powered by NICT】

Fabrication and thermal shock resistance of β-Si₃N₄-based environmental barrier coating on porous Si₃N₄ ceramic

著者 (5件)： Wang Chao (School of Material Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning 110870, China) ,  Wang Hongjie (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an, Shannxi 710049, China) ,  Qiao Ruiqing (School of Material Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning 110870, China) ,  Zhang Chunhua (School of Material Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning 110870, China) ,  Chen Lijia (School of Material Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning 110870, China)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 12  ページ： 14222-14227  発行年： 2016年09月 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 多孔質Si_3N_4セラミック上の液体浸透と充填法を用いて作製した高密度βSi_3N_4ベース防水環境障壁コーティング。被覆の微細構造と耐熱衝撃性を調査した。結果は,コーティングがβSi_3N_4,Y_10Al_2Si_3O_18N_4とY Si Al Oガラスから成っていた。調製されたままの被覆は優れた耐熱衝撃性を示した。ΔT=1200°Cでの熱衝撃の間,亀裂はコーティングの中で形成されたが,それらは被覆の靭性化機構,βSi_3N_4粒子橋架け及び亀裂分岐を含むによる全被覆を通して浸透しなかった。添加では,被覆は,熱サイクル中に良好な亀裂自己封止能力,これは主に亀裂内のβSi_3N_4粒子のガラス流動と酸化に起因しているを示した。25回の熱サイクル後,被覆は良好な防水能力を持ち,被覆多孔質Si_3N_4試料の水吸収は4.5%からわずか9.3%に増加した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 熱サイクル ,  防水 ,  ガラス ,  *熱衝撃 ,  *衝撃強さ ,  亀裂 ,  *多孔質シリコン ,  微細構造 ,  *セラミック ,  靱性 ,  浸透 ,  耐熱衝撃性 ,  *被覆 ,  高密度 ,  *機械的性質 ,  *強度

著者キーワード (5件)： 多孔質Si_3_N_4セラミック ,  βSi_3N_4ベース被覆 ,  水吸収 ,  熱衝撃抵抗 ,  亀裂自己シール性

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (4件)： セラミック ,  コーティング ,  作製 ,  熱衝撃