900 1100°Cでのナノメータ粒径を持つサマリウムドープセリアセラミックの高速ち密化【Powered by NICT】

Rapid densification of Samarium-doped Ceria ceramic with nanometric grain size at 900-1100°C

著者 (5件)： Biesuz Mattia (University of Trento, Department of Industrial Engineering, Via Sommarive, 9, 38123 Trento, Italy) ,  Spiridigliozzi Luca (University of Cassino and Southern Lazio, Department of Civil and Mechanical Engineering, Via Di Biasio 43, 03043 Cassino(FR), Italy) ,  Frasnelli Matteo (University of Trento, Department of Industrial Engineering, Via Sommarive, 9, 38123 Trento, Italy) ,  Dell’Agli Gianfranco (University of Cassino and Southern Lazio, Department of Civil and Mechanical Engineering, Via Di Biasio 43, 03043 Cassino(FR), Italy) ,  Sglavo Vincenzo M. (University of Trento, Department of Industrial Engineering, Via Sommarive, 9, 38123 Trento, Italy)
資料名： Materials Letters  (Materials Letters)
巻： 190  ページ： 17-19  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 10mo1%サマリウムドープセリアナノ粉末は300sにおける迅速焼成によりち密化し,900~1100°Cの温度で予熱した炉を使用している突出した焼結速度は緻密化機構は十分に活性化されることを明らかに達成された。焼結ペレットをナノメータ粒サイズ,ほとんどすべての場合に100nm以下を有していた。も細かい微細構造は焼成温度を増加させることによって得られることを示した。緻密化と結晶粒度に及ぼす高加熱速度プロセスの有益な効果を指摘した30~60秒の浸漬時間を用いた1100°Cでの最適処理条件を定義することを可能にした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 焼結 ,  結晶粒度 ,  ペレット ,  *高速度 ,  加熱速度 ,  予熱 ,  微細構造 ,  *緻密化 ,  *粒径
準シソーラス用語： 浸漬時間 ,  焼成温度 ,  焼結速度 ,  ナノ粉末 ,  *サマリウムドープセリア ,  *ナノメータ , 【Automatic Indexing@JST】

著者キーワード (5件)： SDC ,  迅速焼成 ,  焼結 ,  Nanopowders ,  電解質

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (3件)： ナノメータ ,  粒径 ,  ち密化