ZnFe_2O_4/SiO_2/PESナノろ過膜の調製のための転相中の磁場増強凝固浴:透過流束強化と汚れへの抵抗性のための新しい方法【Powered by NICT】

Magnetic field-augmented coagulation bath during phase inversion for preparation of ZnFe₂O₄/SiO₂/PES nanofiltration membrane: A novel method for flux enhancement and fouling resistance

著者 (4件)： Zinadini S. (Environmental Research Center, Department of Applied Chemistry, Faculty of Chemistry, Razi University, Kermanshah, Iran) ,  Zinatizadeh A.A.L. (Environmental Research Center, Department of Applied Chemistry, Faculty of Chemistry, Razi University, Kermanshah, Iran) ,  Rahimi M. (CFD Research Centre, Department of Chemical Engineering, Faculty of Engineering, Razi University, Kermanshah 67149, Iran) ,  Vatanpour V. (Faculty of Chemistry, Kharazmi University, Tehran, Iran)
資料名： Journal of Industrial and Engineering Chemistry  (Journal of Industrial and Engineering Chemistry)
巻： 46  ページ： 9-18  発行年： 2017年 
JST資料番号： W3170A  ISSN： 1226-086X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ナノ複合材料ポリエーテルスルホン(PES)ナノ濾過膜を相反転法により自己合成磁気ZnFe_2O_4/SiO_2ナノ充填剤を用いて調製した。本論文の主な目的は,調製した膜の特性に及ぼす凝固段階で磁場の影響を調べることであった。作製した混合マトリックス膜の性能を,純水フラックス,塩排除率とファウリングパラメータを測定することにより研究した。結果として,磁場下の凝固浴を1wt.%ZnFe_2O_4/SiO_2ナノ粒子の存在下で膜の純水透過流束を約12kg/m~2H(磁場なし)から38kg/m~2時間にした。これは0.1Tの磁場下で凝固した膜形態,スキン層構造を変えた上の磁性ナノフィラの量によって記述される。EDXマッピングは,磁性ナノ粒子が膜表面,膜は磁場下の凝固時に移動することを示した。水接触角測定は,磁場,粉乳溶液に対して優れた防汚特性をもたらした0.5wt.%ZnFe_2O_4/SiO_2に埋め込まれた膜の優れた親水性を示した。磁場下での0.5wt%ナノ粒子の塩保持配列は,R(Na_2SO_4)>R(MgSO_4)>R(NaCl)の順であった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ナノ粒子 ,  *凝固 ,  磁性 ,  親水性 ,  純水 ,  *透過流束 ,  *ナノ濾過 ,  形態 ,  ナノ複合材料 ,  *磁場
準シソーラス用語： 水接触角 ,  磁性ナノ粒子 ,  水フラックス ,  *転相 ,  *ナノ濾過膜 , 【Automatic Indexing@JST】

著者キーワード (5件)： ナノろ過 ,  混合マトリックス膜 ,  ZnFe_2O_4/SiO_2ナノ粒子 ,  磁場 ,  防汚

分類 (1件)： 膜分離  (XD02120Z)

タイトルに関連する用語 (10件)： ナノろ過膜 ,  調製 ,  転相 ,  磁場 ,  増強 ,  凝固 ,  透過流束 ,  強化 ,  汚れ ,  抵抗性