ニッケル触媒により合成したほう素carbide/carbonセラミック前駆体のためのポリ(フェニレンカルボラン)【Powered by NICT】

Poly(phenylene-carborane) for boron-carbide/carbon ceramic precursor synthesized via nickel catalysis

著者 (6件)： Cheng Shengli (Polymer Science & Materials, Chemical Engineering College, Dalian University of Technology, Dalian, 116024, China) ,  Yuan Kuanyu (Polymer Science & Materials, Chemical Engineering College, Dalian University of Technology, Dalian, 116024, China) ,  Wang Xin (Polymer Science & Materials, Chemical Engineering College, Dalian University of Technology, Dalian, 116024, China) ,  Han Jianhua (Polymer Science & Materials, Chemical Engineering College, Dalian University of Technology, Dalian, 116024, China) ,  Jian Xigao (State Key Laboratory of Fine Chemicals, Dalian University of Technology, Dalian, 116024, China) ,  Wang Jinyan (State Key Laboratory of Fine Chemicals, Dalian University of Technology, Dalian, 116024, China)
資料名： Polymer  (Polymer)
巻： 115  ページ： 224-231  発行年： 2017年 
JST資料番号： D0472B  ISSN： 0032-3861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高熱および熱酸化安定性ポリ(フェニレンカルボラン)(PPB)はカルボランを含むビス(アリール クロリド)単量体のNi(0)触媒重合により合成した。このポリマは,室温でTHF,NMPに可溶であった,分子量と分光分析を可能にした。~1H NMR分光法により決定した数平均分子量は5.4×10~3g/molであった。PPBの結晶特性をXRD分析により確認した。このポリマは窒素及び空気中における707°Cと>1000°Cと5%重量損失温度と共に優れた熱安定性と熱酸化安定性を示した。窒素及び空気中の1000°Cで得られ,それぞれは93.2%と97.9%の高チャー収率。さらに,PPBは91.1%~ 92.6%の範囲の高いセラミック収率を持つセラミック材料をほう素carbide/carbonに優れたsing源前駆体であることが分かった。XRD分析によれば,PPB用炭化ほう素結晶化は1000と1200°Cの間で起こった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 窒素 ,  重合体 ,  炭化ホウ素 ,  *ニッケル触媒 ,  重量損失 ,  分子量 ,  結晶 ,  *セラミック ,  熱安定性 ,  *カルボラン ,  X線回折 ,  *前駆体 ,  チャー ,  塩化物
準シソーラス用語： 酸化安定性 , 【Automatic Indexing@JST】

著者キーワード (3件)： Ni(0)-触媒による重合 ,  ポリ(フェニレンカルボラン) ,  炭化ほう素

分類 (1件)： 重縮合  (CG04050Z)

タイトルに関連する用語 (4件)： ニッケル触媒 ,  ほう素 ,  セラミック ,  前駆体