高フラックスポリアミド逆浸透膜のための高多孔質炭素nanotube/ポリスルホンナノ複合材料支持体【Powered by NICT】

Highly porous carbon nanotube/polysulfone nanocomposite supports for high-flux polyamide reverse osmosis membranes

著者 (6件)： Lee Tae Hoon (Hanyang University, Department of Energy Engineering, Seoul 04763, Republic of Korea) ,  Lee Min Yong (Hanyang University, Department of Energy Engineering, Seoul 04763, Republic of Korea) ,  Lee Hee Dae (Hanyang University, Department of Energy Engineering, Seoul 04763, Republic of Korea) ,  Roh Ji Soo (Hanyang University, Department of Energy Engineering, Seoul 04763, Republic of Korea) ,  Kim Hyo Won (Hanyang University, Department of Energy Engineering, Seoul 04763, Republic of Korea) ,  Park Ho Bum (Hanyang University, Department of Energy Engineering, Seoul 04763, Republic of Korea)
資料名： Journal of Membrane Science  (Journal of Membrane Science)
巻： 539  ページ： 441-450  発行年： 2017年 
JST資料番号： E0669A  ISSN： 0376-7388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 最近の研究では,薄膜複合(TFC)膜の支持層の表面特性を逆浸透(RO)性能に重要な役割を果たしていることを強調している。本研究では,カーボンナノチューブ(CNT)を用いて微多孔質ポリスルホン膜の表面特性を調整した。調製したCNT/PSfナノ複合材料担体は有意に改善された表面多孔性を示した表面細孔径と疎水性の両方を維持した。このような表面特性は,大きな表面積を有するポリアミド(PA)選択層の無欠陥形成,これはPA TFC膜の流束の増大となった。CNT/PSfナノ複合材料担体を用いて調製したPA TFC膜は,裸のPA TFC膜に比べて塩排除率を失うことなく35%まで改善された水透過性を示した。結果は担体の表面多孔性は,TFC膜の水透過性よりもむしろ担体内の純水フラックスまたはPA層の厚さに影響する支配的な因子であることを明らかにした。も担体材料の添加剤としてのCNTsと親水性細孔形成剤の比較研究を通して最適担体を生成するための方向を提案した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 薄膜 ,  *多孔性 ,  支持層 ,  添加剤 ,  *逆浸透膜 ,  表面性状 ,  親水性 ,  細孔径 ,  *ナノ複合材料 ,  透水性 ,  *逆浸透 ,  疎水性
準シソーラス用語： 細孔形成剤 ,  水フラックス ,  ポリスルフォン膜 , 【Automatic Indexing@JST】

著者キーワード (5件)： 逆浸透 ,  脱塩 ,  カーボンナノチューブ ,  担体 ,  高分子ナノ複合材料

分類 (1件)： 膜分離  (XD02120Z)

タイトルに関連する用語 (4件)： 逆浸透膜 ,  多孔質炭素 ,  ポリスルホン ,  ナノ複合材料