9Cr ODS鋼粉末におけるナノ粒子形成のその場SANS研究【Powered by NICT】

An in situ SANS study of nanoparticles formation in 9Cr ODS steel powders

著者 (6件)： He Pei (Institute of Materials, China Academy of Engineering Physics, Mianyang 621908, China) ,  Gao Penglin (Department of Physics, University of Science and Technology Beijing, Beijing 100083, China) ,  Gao Penglin (Key Laboratory of Neutron Physics and Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621999, China) ,  Tian Qiang (Key Laboratory of Neutron Physics and Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621999, China) ,  Lv Jianming (Institute of Materials, China Academy of Engineering Physics, Mianyang 621908, China) ,  Yao Weizhi (Institute of Materials, China Academy of Engineering Physics, Mianyang 621908, China)
資料名： Materials Letters  (Materials Letters)
巻： 209  ページ： 535-538  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ナノ粒子強化の特性は,酸化物分散強化(ODS)鋼の機械的性質と耐放射線性に大きな影響を持っている。in situ小角中性子散乱(SANS)実験は,9Cr ODS鋼粉末温度により変化した中のナノ粒子の進化を決定した。初期付加Y_2O_3はメカニカルアロイング後の鋼マトリックス中に完全に溶解した。ナノ粒子は,10分間の600°Cでのアニーリング後に出現し,12時間後にわずかに粗大化する。ナノ粒子の半径は1000°Cおよび600°Cで0.73nmから1.63nmに増加し,一方体積分率はアニール温度の上昇とともに減少した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *ナノ粒子 ,  耐放射線性 ,  中性子回折 ,  酸化物 ,  メカニカルアロイング ,  *鋼 ,  散乱 ,  分散強化 ,  焼なまし ,  *粉体 ,  機械的性質 ,  体積率
準シソーラス用語： *ODS鋼 , 【Automatic Indexing@JST】

著者キーワード (4件)： Nanoparticles ,  中性子回折と散乱 ,  ODS鋼粉 ,  その場SANS

分類 (3件)： 分散冶金  (WC02040I) ,  分散強化合金  (WE04030R) ,  粉末製造  (WC02020M)

タイトルに関連する用語 (5件)： ODS鋼 ,  粉末 ,  粒子形成 ,  SANS ,  研究