ラングバイナイトK_2Ti_1.887Yb_0.113(PO_4)-3単結晶からのYb~3+の明るい青色協調アップコンバージョン発光【Powered by NICT】

Bright blue cooperative upconversion emission of Yb³⁺ from langbeinite K₂Ti_1.887 Yb_0.113(PO₄)₃ single crystal

著者 (6件)： Sadhasivam S. (Department of Physics, SSN College of Engineering, Tamil Nadu-603 110, India) ,  Sadhasivam S. (Department of Medical Physics, School of Physics, Bharathidasan University, Tamil Nadu-620 024, India) ,  Manivel P. (Department of Medical Physics, School of Physics, Bharathidasan University, Tamil Nadu-620 024, India) ,  Jeganathan K. (Department of Medical Physics, School of Physics, Bharathidasan University, Tamil Nadu-620 024, India) ,  Jayasankar C.K. (Department of Physics, Sri Venkateswara University, Tirupati-517 502, India) ,  Rajesh N.P. (Department of Physics, SSN College of Engineering, Tamil Nadu-603 110, India)
資料名： Materials Letters  (Materials Letters)
巻： 188  ページ： 399-402  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： イッテルビウムをドープしたラングバイナイトK_2Ti_1 0.887Yb_0 113(PO_4)3(KTYP)単結晶を高温溶融塩フラックス成長法を用いて成長させた。3×3×3mm~3までのサイズでは,介在物のないKTYP結晶はK_6P_4O_13溶融フラックスを用いて達成した。溶質と溶媒の完全な融点は1223K以上であった。ラングバイナイト相KTYP結晶をフラックス溶液中Yb_2O_3の高濃度で成長している。KTYPは980nmレーザ励起下でのYb-Yb対による488nmを中心とする強い協同的青色発光を示した。我々の知る限りでは,りん酸塩ラングバイナイト結晶は~488nmの共同アップコンバージョン放出を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： フラックス法 ,  *発光 ,  レーザ励起 ,  溶質 ,  イッテルビウム ,  介在物 ,  *単結晶 ,  融点 ,  ドーピング ,  リン酸塩 ,  *結晶 ,  *周波数逓倍
準シソーラス用語： 青色発光 ,  高濃度 , 【Automatic Indexing@JST】

著者キーワード (4件)： フラックス成長 ,  ルミネセンス ,  光学材料 ,  結晶成長

分類 (1件)： 酸化物の結晶成長  (BK13050I)

タイトルに関連する用語 (4件)： 単結晶 ,  青色 ,  協調 ,  アップコンバージョン