短竹繊維で強化したカリウム-ベースのジオポリマー複合材料【Powered by NICT】

Potassium-Based Geopolymer Composites Reinforced with Chopped Bamboo Fibers

著者 (5件)： Sankar Kaushik (Department of Materials Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, Illinois, 61801) ,  Sa Ribeiro Ruy A. (Department of Materials Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, Illinois, 61801) ,  Sa Ribeiro Ruy A. (Structural Engineering Laboratory, National Institute for Amazonian Research, Manaus, AM, 69067-375, Brazil) ,  Sa Ribeiro Marilene G. (Structural Engineering Laboratory, National Institute for Amazonian Research, Manaus, AM, 69067-375, Brazil) ,  Kriven Waltraud M. (Department of Materials Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, Illinois, 61801)
資料名： Journal of the American Ceramic Society  (Journal of the American Ceramic Society)
巻： 100  号： 1  ページ： 49-55  発行年： 2017年 
JST資料番号： C0253A  ISSN： 0002-7820  CODEN： JACTAW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 竹は鋼のそれ(250 625 MPa/g/cm~3)に相当する引張比強度を有する急速に,容易に入手可能な天然材料である。持続可能な建設材料の追求では,強化材としてアマゾン地域からのマトリックスとランダム配向チョップした竹繊維(Guadua angustifolia)としてのカリウムポリシアレートシロキソジオポリマーを行った複合材料。竹繊維で強化したジオポリマ複合材料の四点曲げ強度試験をASTM標準C78/C78M 10~e1に従って実施した。5wt%(8vo1%)未処理竹繊維で強化したカリウムベースメタカオリンジオポリマーは7.5MPa四点曲げ強さが得られた。走査型電子顕微鏡および光学顕微鏡を用いて,微細構造を調べた。さらに,X線回折は,ジオポリマーの形成を確認するために使用した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 鋼 ,  走査電子顕微鏡 ,  天然材料 ,  引張 ,  光学顕微鏡 ,  *複合材料 ,  曲げ強さ ,  微細構造 ,  補強材料 ,  ASTM規格 ,  高速度 ,  X線回折
準シソーラス用語： 比強度 ,  *ジオポリマ ,  *竹繊維 , 【Automatic Indexing@JST】

著者キーワード (5件)： ジオポリマ ,  複合材料 ,  カオリナイト ,  繊維 ,  カリウム

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (5件)： 竹繊維 ,  強化 ,  カリウム ,  ジオポリマー ,  複合材料