八分木トラス格子の破壊靭性【Powered by NICT】

The fracture toughness of octet-truss lattices

著者 (5件)： O’Masta M.R. (Engineering Department, University of Cambridge, Trumpington Street, Cambridge CB2 1PZ, UK) ,  Dong L. (Department of Material Science & Engineering, School of Engineering and Applied Science, University of Virginia, Charlottesville, VA 22904, USA) ,  St-Pierre L. (Engineering Department, University of Cambridge, Trumpington Street, Cambridge CB2 1PZ, UK) ,  Wadley H.N.G. (Department of Material Science & Engineering, School of Engineering and Applied Science, University of Virginia, Charlottesville, VA 22904, USA) ,  Deshpande V.S. (Engineering Department, University of Cambridge, Trumpington Street, Cambridge CB2 1PZ, UK)
資料名： Journal of the Mechanics and Physics of Solids  (Journal of the Mechanics and Physics of Solids)
巻： 98  ページ： 271-289  発行年： 2017年 
JST資料番号： C0320A  ISSN： 0022-5096  CODEN： JMPSA8  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 1000kgm~ 3以下の密度を用いて,高強度と靭性をあわせもつ唯一の技術的材料は天然材料(木材)といくつかのプラスチックである。,強い,低密度金属トラスの周期配列から作られた場合,8重項格子のようなセル状構造は,高い比強度と弾性係数を持つことが知られている。しかし,それらの破壊までの抵抗のほとんど知られていない。ここでは,「スナップフィット法を用いて製造したTi-6Al-4V合金8重項格子トラス構造の破壊靭性を調べた。試料は360と855kgm~ 3(相対密度8 19%)の密度と自由トラス長さ4および15mmの間であった。それらの破壊抵抗は単エッジ切欠き曲げ試験片に対するJ積分の適用コンプライアンス法を用いて決定した。靭性は相対密度とセルサイズの平方根と共に直線的に増加することが示され,一方,強度は相対密度と固体の強度でのみスケールすることを確認した。亀裂長さ(R曲線効果)抵抗性の中程度の増加は高い相対密度とより大きな細胞サイズの試料で見られた。2と14MPam~1/2の間破壊靭性と20と70MPaの間の圧縮強度を用いて,これらの構造が450°Cまでの温度で使用するための新しい軽量エンジニアリング材料解決策を提供するCopyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： J積分 ,  天然材料 ,  圧縮強さ ,  破壊強さ ,  *破壊靱性 ,  コンプライアンス ,  切欠き ,  *トラス ,  曲げ試験 ,  *靱性 ,  相対密度
準シソーラス用語： 亀裂長さ ,  比強度 ,  八重項 ,  高強度 , 【Automatic Indexing@JST】

著者キーワード (4件)： 格子構造 ,  破壊 ,  靱性 ,  チタン合金

分類 (2件)： 破壊力学一般  (HC04010A) ,  セラミック材料  (HC04040H)

タイトルに関連する用語 (3件)： トラス ,  格子 ,  破壊靭性