新しい高Coニッケル基多結晶超合金の結晶粒組織に及ぼすひずみ量と歪速度の影響【Powered by NICT】

Effects of strain amount and strain rate on grain structure of a novel high Co nickel-based polycrystalline superalloy

著者 (22件)： Tan Liming (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Tan Liming (Powder Metallurgy Research Institute, Central South University, Changsha 410083, China) ,  Tan Liming (High Temperature Materials Research Institute, Central South University, Changsha 410083, China) ,  Huang Zaiwang (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Huang Zaiwang (Powder Metallurgy Research Institute, Central South University, Changsha 410083, China) ,  Huang Zaiwang (High Temperature Materials Research Institute, Central South University, Changsha 410083, China) ,  Liu Feng (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Liu Feng (Powder Metallurgy Research Institute, Central South University, Changsha 410083, China) ,  Liu Feng (High Temperature Materials Research Institute, Central South University, Changsha 410083, China) ,  He Guoai (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  He Guoai (Powder Metallurgy Research Institute, Central South University, Changsha 410083, China) ,  He Guoai (High Temperature Materials Research Institute, Central South University, Changsha 410083, China) ,  Wang Xin (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Wang Xin (Powder Metallurgy Research Institute, Central South University, Changsha 410083, China) ,  Wang Xin (High Temperature Materials Research Institute, Central South University, Changsha 410083, China) ,  Huang Lan (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Huang Lan (Powder Metallurgy Research Institute, Central South University, Changsha 410083, China) ,  Huang Lan (High Temperature Materials Research Institute, Central South University, Changsha 410083, China) ,  Zhang Yiwen (High Temperature Material Institute, Central Iron and Steel Research Institute, Beijing 100081, China) ,  Jiang Liang (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Jiang Liang (Powder Metallurgy Research Institute, Central South University, Changsha 410083, China) ,  Jiang Liang (High Temperature Materials Research Institute, Central South University, Changsha 410083, China)
資料名： Materials & Design  (Materials & Design)
巻： 131  ページ： 60-68  発行年： 2017年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高Coを添加したニッケル基超合金の開発が最近ガスタービンの高温部におけるそれらの潜在的応用のために広く関心を呼んでいる。しかし,作動パラメータは,これらの超合金の結晶粒発展にどのように影響するか高温系統的に研究されていない。本研究では,熱間圧縮後の単一試料の異なる領域での勾配歪を生成した,ハイスループット二重円錐(DC)試験片は,新しい超合金の熱機械的挙動を検討するためにデザインした。Superslovus処理はその後異常粒成長(AGG)に対する感受性を調べるために行われた。有限要素シミュレーション,透過型電子顕微鏡(TEM),および電子後方散乱回折(EBSD)を用いて,遅い歪DCはスーパーソルバス焼なまし後の良く分散した結晶粒構造を得るために,変形中のその適切な動的再結晶(DRX)と動的回復(DRV)のために好ましいことが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *超合金 ,  動的回復 ,  ガスタービン ,  高温 ,  *ニッケル ,  焼なまし ,  *歪速度 ,  ニッケル合金 ,  *結晶粒 ,  *多結晶 ,  動的再結晶 ,  透過型電子顕微鏡
準シソーラス用語： EBSD ,  有限要素シミュレーション ,  異常粒成長 ,  ニッケル基超合金 , 【Automatic Indexing@JST】

著者キーワード (5件)： 高Co添加 ,  ニッケル基超合金 ,  動的再結晶 ,  動的回復 ,  異常結晶粒成長

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： CO ,  ニッケル基 ,  多結晶 ,  超合金 ,  結晶粒組織 ,  ひずみ量 ,  歪速度