AZ31マグネシウム合金7A04アルミニウム合金の異種慣性摩擦溶接のミクロ組織と機械的性質【Powered by NICT】

Microstructure and mechanical properties of dissimilar inertia friction welding of 7A04 aluminum alloy to AZ31 magnesium alloy

著者 (5件)： Guo Wei (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China) ,  You Guoqiang (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China) ,  You Guoqiang (National Engineering Research Center for Magnesium Alloys, Chongqing University, Chongqing, 400044, China) ,  Yuan Guangyu (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China) ,  Zhang Xiuli (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 695  ページ： 3267-3277  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 7A04アルミニウム合金棒とAZ31マグネシウム合金棒の間の異材継手は慣性摩擦溶接法で作製した。継手のミクロ組織と機械的性質に及ぼす摩擦圧力の影響を調べた。結果は,主にAl_12Mg_17とAl_3Mg_2,金属間化合物(IMC)が界面で形成されたことを示した。大量微小亀裂はIMC中間層中に生成した。IMC層の厚さは摩擦圧力の増加と共に有意に減少した。機械的性質を引張試験と微小硬さで評価した。継手の機械的性質は,界面でのIMC中間層の特性である。継手の引張強さは摩擦圧力の増加と共に著しく増加した。96MPaの最大引張強さは124MPaの摩擦圧力下で達成した。すべての引張試験片はIMC中間層とAl母材の間の境界に沿って準劈開破壊モードで破壊した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *アルミニウム ,  金属間化合物 ,  引張試験 ,  界面 ,  微小硬さ ,  *摩擦溶接 ,  *マグネシウム合金 ,  微小亀裂 ,  引張強さ ,  *機械的性質 ,  *アルミニウム合金
準シソーラス用語： 劈開破壊 ,  中間層 ,  *AZ31 , 【Automatic Indexing@JST】

著者キーワード (6件)： イナーシャ摩擦溶接 ,  アルミニウム合金棒 ,  マグネシウム合金棒 ,  Microstructure ,  引張強さ ,  破壊形態

分類 (2件)： ろう付  (WC07050C) ,  溶接部  (WC07100I)

タイトルに関連する用語 (6件)： AZ31マグネシウム合金 ,  アルミニウム合金 ,  慣性 ,  摩擦溶接 ,  ミクロ組織 ,  機械的性質