対向材料W La_2O_3合金候補プラズマにおけるHe照射中のD_2保持と微細構造の進展【Powered by NICT】

D₂ retention and microstructural evolution during He irradiation in candidate plasma facing material W-La₂O₃ alloy

著者 (7件)： Xu Q. (Research Reactor Institute, Kyoto University, Osaka 590-0494, Japan) ,  Ding X.Y. (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230031, China) ,  Luo L.M. (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230031, China) ,  Miyamoto M. (Shimane University, Shimane 690-8504, Japan) ,  Tokitani M. (National Institute for Fusion Science, Gifu 509-5292, Japan) ,  Zhang J. (Research Reactor Institute, Kyoto University, Osaka 590-0494, Japan) ,  Wu Y.C. (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230031, China)
資料名： Journal of Nuclear Materials  (Journal of Nuclear Materials)
巻： 496  ページ： 227-233  発行年： 2017年 
JST資料番号： D0148A  ISSN： 0022-3115  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 分散強化W合金,W La_2O_3,スパークプラズマ焼結(SPS)によって開発した。高温で5-KeV He照射下でD_2保持と微構造発達を調べた。W La_2O_3合金の密度は市販のWのそれより低いが,D_2保持は有意に変化しなかった。さらに,市販Wでは見られない,D_2熱脱着ピークはDからの解離空格子点クラスタに起因する~700Kで現れた。W La_2O_3では,Heバブルの形成は,773K,973Kと1173Kで観察された。照射温度が上昇すると,ボイドスエリングも増加した。同じ温度では,Heバブルの形成は,商業用WよりもW La_2O_3容易にこれはW La_2O_3の低密度の原因と考えられている。W La_2O_3はHe照射前に空格子点の高い密度を持っていた。第二相としてLa_2O_3の分散により誘起された空格子点凝集の抑制は高照射線量でのみ出現した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *合金 ,  *プラズマ ,  *ヘリウム ,  第二相 ,  クラスタ ,  タングステン合金 ,  分散強化 ,  放電プラズマ焼結 ,  気泡 ,  照射線量 ,  熱脱着 ,  ボイドスエリング ,  高温 ,  凝集
準シソーラス用語： 構造進化 , 【Automatic Indexing@JST】

著者キーワード (4件)： W La_2O_3 ,  D_2照射 ,  He照射 ,  He気泡

分類 (3件)： 核融合装置  (BJ02083Z) ,  固体-プラズマ相互作用  (BJ02033W) ,  金属の格子欠陥  (BK12030F)

タイトルに関連する用語 (5件)： 合金 ,  プラズマ ,  He ,  微細構造 ,  進展