J-GLOBAL ID：201702262243533756   整理番号：17A0453229

Cu-Ce-Zr担持ZSM-5/TiO_2/Al_2O_3を用いた誘電体バリア放電結合によるトルエンの除去強化【Powered by NICT】

Enhanced removal of toluene by dielectric barrier discharge coupling with Cu-Ce-Zr supported ZSM-5/TiO₂/Al₂O₃

著者 (7件)： Dou Baojuan (Tianjin University of Science & Technology, Tianjin 300457, China) ,  Liu Deliang (Tianjin University of Science & Technology, Tianjin 300457, China) ,  Zhang Qing (Tianjin University of Science & Technology, Tianjin 300457, China) ,  Zhao Ruozhu (Tianjin University of Science & Technology, Tianjin 300457, China) ,  Hao Qinglan (Tianjin University of Science & Technology, Tianjin 300457, China) ,  Bin Feng (State Key Laboratory of High-Temperature Gas Dynamics, Institute of Mechanics, Chinese Academy of Sciences, Beijing 100190, China) ,  Cao Jingguo (Tianjin University of Science & Technology, Tianjin 300457, China)
資料名： Catalysis Communications  (Catalysis Communications)
巻： 92  ページ： 15-18  発行年： 2017年 
JST資料番号： W1328A  ISSN： 1566-7367  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： トルエンはCu-Ce-Zr担持ZSM-5/TiO_2/Al_2O_3触媒による誘電体バリア放電結合によって除去された。銅,セリウムおよびジルコニウム種は担体表面上に高度に分散し,銅は大部分がCu~2+及びCu~+状態の共存。プラズマ-触媒系におけるトルエン除去の反応過程を触媒の担体に影響され,それは三段階に分けることができた。背景温度により誘発された純粋なプラズマおよび熱触媒化学は異なる段階で異なる役割をplaid。CuCeZr/TiO_2の大きな細孔径,より多くの酸素空孔と格子酸素は優れていたトルエン除去,CO_2選択性とエネルギー収率の原因である。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *銅 ,  *無声放電 ,  *セリウム ,  *ジルコニウム ,  細孔径 ,  触媒 ,  プラズマ ,  アルキルベンゼン
準シソーラス用語： エネルギー収率 ,  格子酸素 ,  酸素空格子点 ,  触媒化学 ,  反応過程 , 【Automatic Indexing@JST】

著者キーワード (4件)： 誘電体バリア放電 ,  Cu-Ce-Zr触媒 ,  触媒のキャラクタリゼーション ,  トルエン

分類 (2件)： その他の触媒  (CB06123Z) ,  不均一系触媒反応  (CB06100E)

物質索引 (1件)： トルエン

タイトルに関連する用語 (8件)： Cu ,  Ce ,  Zr ,  担持 ,  ZSM-5 ,  誘電体バリア放電 ,  トルエン ,  強化