J-GLOBAL ID：201702262592429987   整理番号：17A1056847

化学液相-気相浸透法で作製した同時蒸着ZrC修飾したC/C複合材料の酸化挙動【Powered by NICT】

Oxidation behavior of co-deposited ZrC modified C/C composites prepared by chemical liquid-vapor infiltration process

著者 (4件)： He Qinchuan (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an 710072, China) ,  Li Hejun (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an 710072, China) ,  Lu Jinhua (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an 710072, China) ,  Li Wei (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an 710072, China)
資料名： Vacuum  (Vacuum)
巻： 142  ページ： 154-163  発行年： 2017年 
JST資料番号： E0347A  ISSN： 0042-207X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 化学液体-蒸気浸透法(CLVI)法で作製したC/C-ZrC複合材料の酸化挙動を研究し,耐酸化性に同時蒸着したZrCの影響についても考察した。結果はC/C-ZrC複合材料の優れた耐酸化性は,共電着したZrCの導入により得られたことを示した。900°Cで240分酸化後,C/C-ZrC複合材料の重量損失は11.77%に達し,これはC/C複合材料(90.74%)に比べて著しく減少した。炭素繊維に同時蒸着したZrCセラミックスは酸化欠陥の量を減少させるための繊維/マトリックス界面とマトリックスの耐酸化性を改善することができる。ZrO_2層はZrCの酸化保護膜を形成エロージョン攻撃を減少させるにより生成した。図式はC/C-ZrC複合材料の酸化挙動を説明するために提案した。さらに,ZrCの共析出が高い黒鉛化度C/C複合材料をもたらし,複合材料の活性化エネルギー,酸化抵抗特性を改善することを増加させた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 重量損失 ,  *同時蒸着 ,  耐酸化性 ,  黒鉛化 ,  炭素繊維 ,  *C/C複合材料 ,  保護膜 ,  電着 ,  活性化エネルギー ,  セラミック ,  *酸化 ,  *浸透 ,  界面 ,  *複合材料
準シソーラス用語： *酸化挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： C/C複合材料 ,  Microstructure ,  酸化挙動 ,  化学液相-気相浸透

分類 (4件)： 防食  (WB03040M) ,  その他の無機化合物の薄膜  (BK14060A) ,  非金属材料へのセラミック被覆  (YC02040K) ,  炭素とその化合物  (YB02060D)

タイトルに関連する用語 (9件)： 化学 ,  液相 ,  気相 ,  浸透 ,  作製 ,  同時蒸着 ,  修飾 ,  複合材料 ,  酸化挙動