織物炭素/ガラスハイブリッド複合材料の貫通衝撃挙動のための経椎弓破壊靭性の重要性【Powered by NICT】

The importance of translaminar fracture toughness for the penetration impact behaviour of woven carbon/glass hybrid composites

著者 (5件)： Swolfs Yentl (Department of Materials Engineering, KU Leuven, Kasteelpark Arenberg 44 bus, 2450, Belgium) ,  Swolfs Yentl (Department of Aeronautics, Imperial College London, South Kensington Campus, SW7 2AZ London, United Kingdom) ,  Geboes Yoran (Department of Materials Engineering, KU Leuven, Kasteelpark Arenberg 44 bus, 2450, Belgium) ,  Gorbatikh Larissa (Department of Materials Engineering, KU Leuven, Kasteelpark Arenberg 44 bus, 2450, Belgium) ,  Pinho Silvestre T. (Department of Aeronautics, Imperial College London, South Kensington Campus, SW7 2AZ London, United Kingdom)
資料名： Composites. Part A. Applied Science and Manufacturing  (Composites. Part A. Applied Science and Manufacturing)
巻： 103  ページ： 1-8  発行年： 2017年 
JST資料番号： E0231D  ISSN： 1359-835X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 繊維強化複合材料の耐衝撃性は多くの応用において重要であると,繊維ハイブリダイゼーションにおける相乗効果を利用することによって改善することができる。これらの効果は,文献で十分に理解,がされていない。,炭素/ガラスハイブリッドを行った貫通衝撃試験の結果は,曲げ挙動と層間破壊靭性と関連していた。結果は,線形混合則と比較して最大40%の大きな相乗効果を明らかにした。結果は層間破壊表面を生成する時の侵入影響:全炭素繊維複合材料のための56%と全ガラス繊維複合材料の13%吸収エネルギーに強く寄与することができることを明らかにした最初である。これらの結果は,層間破壊靭性を最大化するための戦略も繊維ハイブリッドの浸透耐衝撃性を最大化するために利用できることを証明した。特に炭素繊維複合材料では,プライブロッキング,大きな糸を用い,マイクロカットを導入し,浸透耐衝撃性を増加すべきである。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *ガラス ,  *ハイブリッド複合材料 ,  ガラス繊維 ,  混合則 ,  衝撃強さ ,  相乗作用 ,  破面 ,  浸透 ,  *複合材料 ,  炭素繊維 ,  衝撃試験 ,  *破壊靱性
準シソーラス用語： 層間破壊靱性 ,  繊維強化複合材料 ,  *衝撃挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： Aハイブリッド ,  A高分子マトリックス複合材料(PMCs) ,  B破壊靭性 ,  B衝撃挙動