コールタールピッチとナノMgOの混合物からの多孔質炭素の微細構造に及ぼす炭素熱還元の影響【Powered by NICT】

Effect of carbothermal reduction on the microstructures of porous carbons from the mixture of coal-tar pitch and nano-MgO

著者 (6件)： Zhang Xialan (College of Materials Science and Engineering, Fuzhou University, Fuzhou 350116, PR China) ,  Luo Shiyuan (College of Materials Science and Engineering, Fuzhou University, Fuzhou 350116, PR China) ,  Lin Qilang (College of Materials Science and Engineering, Fuzhou University, Fuzhou 350116, PR China) ,  Wang Yanmao (College of Materials Science and Engineering, Fuzhou University, Fuzhou 350116, PR China) ,  Huang Xiangdong (College of Materials Science and Engineering, Fuzhou University, Fuzhou 350116, PR China) ,  Xiong Lei (College of Materials Science and Engineering, Fuzhou University, Fuzhou 350116, PR China)
資料名： Journal of Analytical and Applied Pyrolysis  (Journal of Analytical and Applied Pyrolysis)
巻： 124  ページ： 73-78  発行年： 2017年 
JST資料番号： B0809A  ISSN： 0165-2370  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 多孔質炭素は,コールタールピッチ及びナノMgOの混合物の熱分解により調製し,ナノMgOの間の炭素熱還元とそれらのミクロ組織に及ぼす炭素の影響を調べた。混合物の熱分解挙動を同時熱重量分析-示差走査熱量測定(TG DSC)とX線回折(XRD)によって特性化した。さらに,得られた多孔質炭素の微細構造を走査電子顕微鏡(SEM),透過型電子顕微鏡(TEM),Raman分光法および窒素吸着-脱着測定を用いて研究した。結果は,温度が1300°Cを越えたときに,炭素熱還元が起こることを示し,得られた多孔質炭素の微細構造に大きく影響を及ぼした。温度の増加と共に,調製した多孔質炭素はメソ細孔容積と細孔壁と高い比表面積の薄い厚さを有していた。温度が1800°Cに達すると,調製した多孔質炭素は,数層グラフェンシートから成る三次元ネットワーク構造を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 走査電子顕微鏡 ,  示差走査熱量測定 ,  *酸化マグネシウム ,  グラフェン ,  熱分解 ,  Raman分光法 ,  *炭素 ,  細孔 ,  *微細構造 ,  ネットワーク構造 ,  熱重量分析
準シソーラス用語： メソ孔 ,  窒素吸着 ,  *炭素熱還元 ,  *多孔質炭素 , 【Automatic Indexing@JST】

著者キーワード (5件)： コールタールピッチ ,  多孔質炭素 ,  炭素熱還元 ,  Microstructures ,  熱分解