透明電極と加熱器のための銅ナノワイヤの水溶液合成と沈着を調整【Powered by NICT】

Tailoring the Aqueous Synthesis and Deposition of Copper Nanowires for Transparent Electrodes and Heaters

著者 (6件)： Bobinger Marco (Department of Electrical and Computer Engineering, Technical University of Munich, Theresienstr. 90, 80333, Munich, Germany) ,  Mock Josef (Department of Electrical and Computer Engineering, Technical University of Munich, Theresienstr. 90, 80333, Munich, Germany) ,  La Torraca Paolo (Dipartimento di Scienze e Metodi dell’Ingegneria, UNIMORE, Via Universita 4, 41121, Modena, Italy) ,  Becherer Markus (Department of Electrical and Computer Engineering, Technical University of Munich, Theresienstr. 90, 80333, Munich, Germany) ,  Lugli Paolo (Faculty of Science and Technology, Free University of Bozen-Bolzano, Universitaetsplatz 1, 39100, Bozen-Bolzano, Italy) ,  Larcher Luca (Dipartimento di Scienze e Metodi dell’Ingegneria, UNIMORE, Via Universita 4, 41121, Modena, Italy)
資料名： Advanced Materials Interfaces  (Advanced Materials Interfaces)
巻： 4  号： 20  ページ： ROMBUNNO.201700568  発行年： 2017年 
JST資料番号： W2484A  ISSN： 2196-7350  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 地球とその高い固有電気伝導率に及ぼす銅の高い豊度のために,銅ナノワイヤ(CuNWs)は透明電極用の有望な材料を代表する。本研究では,低プロセス温度を必要とする環境に優しいかつスケーラブルな合成を研究した。最適温度は79°Cで見られ,これは最低直径を持つナノワイヤが得られた。合成溶液はプロピオン酸と透明導電膜,熱焼結または洗浄のような種々の後処理を受けるのに溶射したその電気光学性能を向上させることである。合成と後処理のための最適プロトコルの両方に続いて,83.4%の透明度で10.3Ω/□~ 1のシート抵抗を達成した。CuNW膜は透明ヒータとして試験し,均一な熱分布を示した。膜の電気的性質のために,バルク銅のものと比較して約28%低下することを抵抗の温度依存性を見出した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 焼結 ,  シート抵抗 ,  *ナノワイヤ ,  電気的性質 ,  *水溶液 ,  温度依存性 ,  *沈着 ,  *銅 ,  溶射 ,  *加熱器 ,  透明導電膜 ,  電気伝導率 ,  *透明電極 ,  透明度 ,  後処理

著者キーワード (4件)： 銅ナノワイヤ(CuNWs) ,  ヒータ ,  合成 ,  透明電極

分類 (2件)： 固体デバイス材料  (NC03020K) ,  固体デバイス製造技術一般  (NC03030V)

タイトルに関連する用語 (6件)： 透明電極 ,  加熱器 ,  銅 ,  ナノワイヤ ,  水溶液 ,  沈着