低駆動場の下でのBi_0(Na_0 78K_0 22)_0.5TiO_3Bi(Mg_0 5Ti_0)O_3系複合セラミックスの大きな歪【Powered by NICT】

Large strain in Bi_0.5(Na_0.78K_0.22)_0.5TiO₃-Bi(Mg_0.5Ti_0.5)O₃ based composite ceramics under low driving field

著者 (6件)： Khaliq Abdul (Department of Physics and EHSRC, University of Ulsan, Ulsan 44610, South Korea) ,  Sheeraz Muhammad (Department of Physics and EHSRC, University of Ulsan, Ulsan 44610, South Korea) ,  Ullah Aman (Department of Physics, University of Science and Technology, Bannu, KP, Pakistan) ,  Lee Jae Shin (School of Materials Science and Engineering, University of Ulsan, Ulsan, South Korea) ,  Ahn Chang Won (Department of Physics and EHSRC, University of Ulsan, Ulsan 44610, South Korea) ,  Kim Ill Won (Department of Physics and EHSRC, University of Ulsan, Ulsan 44610, South Korea)
資料名： Sensors and Actuators. A. Physical  (Sensors and Actuators. A. Physical)
巻： 258  ページ： 174-181  発行年： 2017年 
JST資料番号： B0345C  ISSN： 0924-4247  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 作製したリラクサ/強誘電体複合材料を添加したBi_0 5Na_0 5TiO_3(BNT)種子の重量含有量に依存してリラクサおよび/または強誘電相を示した。Bi_0 5Na_4 5Ti_4O_15大粒子は前駆体として処理し,二重溶融塩法によるBNT板状粒子に修飾した。母材0.96Bi_0(Na_0 0.78K_0 22)0.5TiO_3 0.04Bi(Mg_0 5Ti_0)O_3(BNKT 0.04BMT)を固相反応法により合成した。BNKT-0.04BMT粉末及びBNT種子の0 3型複合材料はペロブスカイト構造間の相溶性のために選択した。BNTペロブスカイト種子は塩基BNKT-0.04BMTマトリックス粉末に1015および20wt%の割合で添加した。添加BNT種子(20wt%)の最高含量は強誘電挙動を示すことをBNKT-0.04BMTを得た。大電場誘起正規化歪(S_max/E_max=560pm/V)は15wt%BNT種子組成のための2.5kV/mmの低駆動場で証明された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 相溶性 ,  強誘電体 ,  固相反応 ,  *駆動場 ,  電場 ,  複合材料 ,  粉体 ,  正規化 ,  前駆体 ,  リラクサ ,  融解塩
準シソーラス用語： ペロブスカイト型構造 ,  *セラミックス複合材料 , 【Automatic Indexing@JST】

著者キーワード (5件)： Piezoelectrics ,  ビスマスチタン酸ナトリウム ,  ペロブスカイト種子 ,  BNKT O-0.04BMT ,  リラクサ強誘電複合材料