Al-Cu-Li合金におけるT_1析出物の形成機構に関する研究【Powered by NICT】

Investigation on formation mechanism of T₁ precipitate in an Al-Cu-Li alloy

著者 (6件)： Deng Yanjun (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Bai Jianhui (Institute for Structure and Function and Department of Physics, Chongqing University, Chongqing, 400044, China) ,  Wu Xiaodong (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Huang Guangjie (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Cao Lingfei (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Huang Li (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 723  ページ： 661-666  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Al-Cu-Li合金におけるT_1(Al_2CuLi)析出物の形成機構を,高角度環状暗視野走査透過型電子顕微鏡(HAADF STEM)イメージング,原子プローブトモグラフィー(APT)と第一原理エネルギー計算を用いて調べた。HAADF-STEM像はT_1前駆体相の存在であり,それは本研究でT_1pと呼ばれるを明らかにした。T_1p相はAlマトリックスに同一の格子構造を持ち,{111}Al面に沿ってLiリッチとCuリッチ層の積層から構成されている。APT解析はさらにT_1p相の存在,LiとCuの濃度はT_1板のそれらより有意に低かったを確認した。第一原理エネルギー計算に基づいて,T1相へT_1p相からの構造進展はエネルギー的に有利であることを証明した。これに対応して,積層順序の変化を含むT_1相へT_1p相から一つの可能な進化プロセスを提案し,議論した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *リチウム ,  単相 ,  前駆体 ,  画像処理 ,  *銅 ,  第一原理 ,  *リチウム合金 ,  *アルミニウム ,  エネルギー計算 ,  *析出物 ,  格子構造
準シソーラス用語： HAADF-STEM ,  原子プローブトモグラフィー ,  暗視野 ,  *形成機構 , 【Automatic Indexing@JST】

著者キーワード (4件)： Al-Cu-Li合金 ,  T_1析出物 ,  前駆体 ,  HAADF-STEM