Fracture behavior of nanostructured heavily cold drawn pearlitic steel wires before and after annealing

著者 (7件)： Jaya B.N. (Max Planck Institut fuer Eisenforschung GmbH, Duesseldorf, Germany) ,  Goto S. (Max Planck Institut fuer Eisenforschung GmbH, Duesseldorf, Germany) ,  Goto S. (Akita University, Tegata Gakuencho, Akita 010-8502, Japan) ,  Richter G. (Max Planck Institute for Intelligent Systems, Stuttgart, Germany) ,  Kirchlechner C. (Max Planck Institut fuer Eisenforschung GmbH, Duesseldorf, Germany) ,  Kirchlechner C. (Department of Material Physics, University of Leoben, Leoben, Austria) ,  Dehm G. (Max Planck Institut fuer Eisenforschung GmbH, Duesseldorf, Germany)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 707  ページ： 164-171  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： in situ微小片持梁破壊試験は引抜歪および焼なまし条件の関数としてナノ構造,強冷間引抜パーライト鋼線の破壊挙動の変化を示すために用いた。はこれらの鋼は7.5~4MPam~~1/2破壊靭性の低下と320%と520%の延伸歪の間の破壊挙動における鋭い遷移を示すことが分かった。は320%以下の歪絞りにおける塑性のいくらかの自由度を持つ安定な破壊の性質から確認され,420%以上の引抜歪で壊滅的劈開破壊に変化した。転移と関連する脆性はこれらの鋼は,より高い引抜き歪で形成する構造(セメンタイト分解と歪誘起増加正方晶)と微細構造(増加ナノ結晶性と転位密度)の変化に起因した。420%歪試料の熱処理について,脆性へき開破壊はミクロ構造が明らかな変化とアニーリングない低温度(200°C)持続するが,亀裂成長は抑制され,大規模塑性は結晶粒粗大化と高温アニーリング(500°C),および結晶粒界での球状化セメンタイトの再析出のために回収した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 破壊靱性 ,  *冷間引抜 ,  微細構造 ,  *共析鋼 ,  低温 ,  脆性 ,  *ナノ構造 ,  結晶粒界 ,  ナノ結晶 ,  亀裂伝搬 ,  セメンタイト ,  *焼なまし ,  結晶粒粗大化 ,  塑性
準シソーラス用語： *破壊挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： パーライト鋼 ,  ナノ結晶 ,  線引 ,  破壊 ,  微視力学

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： アニーリング ,  構造強度 ,  冷間引抜 ,  パーライト鋼 ,  破壊挙動