マロン酸官能化グラフェンと評価その透過性能のから集合した膜の作製【Powered by NICT】

Fabrication of assembled membrane from malonate-functionalized graphene and evaluation of its permeation performance

著者 (5件)： Le Linh Hoang (School of Materials Science, Japan Advanced Institute of Science and Technology, 1-1 Asahidai, Nomi, Ishikawa 923-1292, Japan) ,  Trinh Dai Xuan (School of Materials Science, Japan Advanced Institute of Science and Technology, 1-1 Asahidai, Nomi, Ishikawa 923-1292, Japan) ,  Trung Nguyen Ba (Faculty of Chemistry, University of Education, The University of Danang, 459 Ton Duc Thang, Lien Chieu District, Da Nang, Viet Nam) ,  Tran Thuy Phuong Nhat (School of Materials Science, Japan Advanced Institute of Science and Technology, 1-1 Asahidai, Nomi, Ishikawa 923-1292, Japan) ,  Taniike Toshiaki (School of Materials Science, Japan Advanced Institute of Science and Technology, 1-1 Asahidai, Nomi, Ishikawa 923-1292, Japan)
資料名： Carbon  (Carbon)
巻： 114  ページ： 519-525  発行年： 2017年 
JST資料番号： H0270B  ISSN： 0008-6223  CODEN： CRBNA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： グラフェン膜に関する研究の数の増加は,分離用のグラフェンの大きな可能性を示した。初めて,本研究は官能化グラフェンシートを集合することを新しいグラフェン膜の液体透過性能を示した。官能化グラフェンはブロモマロン酸ジエチルを用いたBingel反応に基づくグラフェン分散から合成し,真空ろ過法を用いて組立てられた膜を調製した。このように調製した膜は,四種の溶媒(ヘキサン,アセトン,メタノールおよび水)を用いた透過試験を行った。化学的官能化は二つの興味深い結果をもたらした:1)も比較的小さい程度の官能化は膜の化学的選択性を劇的に変化し,ii)膜の透過性は大きく強化され,未処理のものに比べて官能化グラフェンシートの規則性の低い積層から発生したもっともらしく。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 規則度 ,  *官能化 ,  真空濾過 ,  *グラフェン ,  脂肪族アルコール ,  脂肪族ケトン ,  脂肪族カルボン酸 ,  ジカルボン酸
準シソーラス用語： Bingel反応 ,  *透過性 , 【Automatic Indexing@JST】

分類 (1件)： 炭素とその化合物  (YB02060D)

物質索引 (3件)： メタノール ,  アセトン ,  マロン酸

タイトルに関連する用語 (7件)： マロン酸 ,  官能化 ,  グラフェン ,  評価 ,  透過性能 ,  集合 ,  作製