ショートフロー圧延プロセスを用いたAZ91O4Snマグネシウム合金における微細粒組織と超塑性【Powered by NICT】

Achieving fine grain structure and superplasticity in AZ91-0.4Sn magnesium alloy using short flow rolling process

著者 (10件)： Yu Zhao-Peng (Key Laboratory of Automobile Materials of Ministry of Education & School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Zha Min (State Key Laboratory of Automotive Simulation and Control, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Zha Min (Key Laboratory of Automobile Materials of Ministry of Education & School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Li Zi-Hao (Key Laboratory of Automobile Materials of Ministry of Education & School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Wang Cheng (State Key Laboratory of Automotive Simulation and Control, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Wang Cheng (Key Laboratory of Automobile Materials of Ministry of Education & School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Wang Hui-Yuan (State Key Laboratory of Automotive Simulation and Control, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Wang Hui-Yuan (Key Laboratory of Automobile Materials of Ministry of Education & School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Jiang Qi-Chuan (State Key Laboratory of Automotive Simulation and Control, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Jiang Qi-Chuan (Key Laboratory of Automobile Materials of Ministry of Education & School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 695  ページ： 1-5  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 硬板圧延の1パスおよび二パス従来の圧延を組み合わせた新しい圧延法を報告した。このルートは,3圧延パスにより約86.4%の総圧下率後のAZ91 4Sn板の弱体化した集合組織を特徴とする球状Mg_17Al_12相(0.5μm)と均一な微細粒組織(3μm)を達成するのに有効である。さらに,処理した合金は200°Cで~96%の超塑性状の破壊歪を示し,Mg_17Al_12の高い体積分率と分散した微細なα-Mg結晶粒によるものであった。この新しいルートは,圧延パスを有意に減少させ,工業生産に大きな可能性を持つ。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶粒 ,  板圧延 ,  *合金 ,  *圧延 ,  工業生産 ,  圧下率 ,  *マグネシウム合金 ,  体積率 ,  *超塑性 ,  集合組織
準シソーラス用語： 引張特性 ,  破壊歪 ,  *AZ91 , 【Automatic Indexing@JST】

著者キーワード (5件)： マグネシウム合金 ,  Superplasticity ,  圧延 ,  テクスチャ ,  引張特性