電子ビーム表面溶融したNb-Si基合金の熱処理誘起相転移と微構造の発達【Powered by NICT】

Heat treatment induced phase transition and microstructural evolution in electron beam surface melted Nb-Si based alloys

著者 (5件)： Guo Yueling (School of Materials Science and Engineering, Beihang University, Beijing 100191, People’s Republic of China) ,  Jia Lina (School of Materials Science and Engineering, Beihang University, Beijing 100191, People’s Republic of China) ,  Kong Bin (School of Materials Science and Engineering, Beihang University, Beijing 100191, People’s Republic of China) ,  Peng Hui (School of Materials Science and Engineering, Beihang University, Beijing 100191, People’s Republic of China) ,  Zhang Hu (School of Materials Science and Engineering, Beihang University, Beijing 100191, People’s Republic of China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 423  ページ： 417-420  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 電子ビーム表面融解(EBSM)とそれに続く熱処理によって処理されたNb18Si,24Ti,2Cr2Al(at.%)合金の硬さ,相と微細構造の発達を調べた。EBSM実験は,電子ビームに基づく3D印刷システムを用いて行った。結果はNbssとNb_3Si相は著しく微細化したミクロ組織とEBSMを介して得られることを示した。Nb_3Si→Nbss+ααNb_5Si_3の共析反応は5h,1200°Cあるいは1450°Cでの熱処理(HT)によって引き起こされた。成長とαNb_5Si_3粒の粗大化はより高いHT温度で促進された。EBSM合金の硬さは,HTにより著しく低下した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *合金 ,  微細構造 ,  *熱処理 ,  *電子ビーム ,  *相転移 ,  精密化 ,  *表面融解 ,  硬度 ,  共析反応
準シソーラス用語： 三次元印刷 , 【Automatic Indexing@JST】

著者キーワード (5件)： Nb-Si合金 ,  Intermetallics ,  表面融解 ,  急冷凝固 ,  熱処理

分類 (2件)： その他の表面処理  (WC08070F) ,  表面硬化熱処理  (WC03030E)

タイトルに関連する用語 (8件)： 電子ビーム ,  表面溶融 ,  Nb ,  Si基合金 ,  熱処理 ,  誘起 ,  相転移 ,  発達