高性能ポリプロピレン繊維軽量骨材コンクリートの凍結融解抵抗性に及ぼす骨材飽和度の影響【Powered by NICT】

Effect of aggregate saturation degree on the freeze-thaw resistance of high performance polypropylene fiber lightweight aggregate concrete

著者 (5件)： Zhu Cong (College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China) ,  Niu Jiangang (School of Architecture and Civil Engineering, Inner Mongolia University of Science and Technology, Baotou 014010, China) ,  Li Jingjun (College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China) ,  Wan Chaojun (College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China) ,  Peng Jiahui (College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 145  ページ： 367-375  発行年： 2017年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究の目的は,ワーカビリティ,圧縮強度及び耐凍結融解性として高性能ポリプロピレン繊維軽量骨材コンクリート(HPPLWC)のそのような特性に及ぼす軽量骨材(LWA)飽和度の影響を調べることであった。四異なる程度に事前吸水した軽量骨材はこの実験で使用した。結果は以下のことを示した:(1)LWAの増加飽和度は,新鮮な混合物の時間とともにスランプロスを有意に減少させることができた;(2)LWAの異なる飽和度を有する試料の28及び56日の圧縮強度は有意な変化を示さなかった;(3)LWAの湿潤前程度は飽和に近いとき相対動弾性係数が著しく減少した。界面遷移帯(ITZ)のSEM研究に加えて,LWA水吸収量を3日でエトリンジャイト(AFt)および水酸化カルシウム(CH)結晶の成長に役立ったことが観察された。28日間硬化させたときに,LWAの飽和度の変化はITZ形態に明らかな影響を及ぼさなかった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 動弾性係数 ,  *飽和度 ,  水酸化カルシウム ,  *軽量骨材 ,  *ポリプロピレン繊維 ,  界面 ,  ワーカビリティ ,  吸水 ,  漸移帯 ,  圧縮強さ ,  形態 ,  湿潤 ,  エトリンジャイト ,  *凍結融解
準シソーラス用語： *軽量骨材コンクリート , 【Automatic Indexing@JST】

著者キーワード (5件)： 軽量骨材コンクリート ,  凝集体飽和度 ,  圧縮強さ ,  凍結融解抵抗性 ,  界面遷移帯