単層カーボンナノチューブFe_2O_3複合膜をベースにしたフレキシブルガスセンサ【Powered by NICT】

A flexible gas sensor based on single-walled carbon nanotube-Fe₂O₃ composite film

著者 (7件)： Hua Chunfei (School of Physical Engineering, Zhengzhou University, Zhengzhou, Henan 450052, PR China) ,  Shang Yuanyuan (School of Physical Engineering, Zhengzhou University, Zhengzhou, Henan 450052, PR China) ,  Wang Ying (School of Physical Engineering, Zhengzhou University, Zhengzhou, Henan 450052, PR China) ,  Xu Jie (School of Physical Engineering, Zhengzhou University, Zhengzhou, Henan 450052, PR China) ,  Zhang Yingjiu (School of Physical Engineering, Zhengzhou University, Zhengzhou, Henan 450052, PR China) ,  Li Xinjian (School of Physical Engineering, Zhengzhou University, Zhengzhou, Henan 450052, PR China) ,  Cao Anyuan (Department of Materials Science and Engineering, College of Engineering, Peking University, Beijing 100871, PR China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 405  ページ： 405-411  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 単層カーボンナノチューブ(SWNT)は,高性能ガスセンサを作成するための可能性を有しているが,検出できることをガスの数はまだ限られていると感度は更なる改善が必要である。ここでは,化学蒸着により直接合成した大面積SWNT膜をNH_3,NO,NO_2のような毒性ガスの範囲のためのガスセンサに構成される。特に,簡単なアニーリング工程を経て得られたSWNT Fe_2O_3複合膜はH_2Sに安定な応答を生成し,NO_2と室温での向上した感度を示し,元のSWNT膜と比較した。多孔質膜均一Fe_2O_3ナノ粒子の形成はよりガスへの性能改善と可能センシングの原因であり,化学的官能化またはドーピングのような従来の段階を除去する。繰り返し大角度に曲げることができるフレキシブルセンサも実証した。大量残留触媒を含むSWNT膜は,種々の毒性ガスのための大面積,フレキシブルな,または着用可能な,薄膜または繊維配置センサに製造できた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 化学蒸着 ,  薄膜 ,  有害ガス ,  官能化 ,  *センサ ,  焼なまし ,  *複合膜 ,  触媒 ,  *単層カーボンナノチューブ ,  ナノ粒子 ,  *ガスセンサ
準シソーラス用語： 多孔質膜 ,  大面積 ,  直接合成 , 【Automatic Indexing@JST】

著者キーワード (4件)： 単層カーボンナノチューブ膜 ,  Fe_2O_3 ,  H_2S ,  ガスセンサ

分類 (2件)： 分析機器  (CC02020S) ,  酸化物薄膜  (BK14050P)

タイトルに関連する用語 (3件)： 単層カーボンナノチューブ ,  複合膜 ,  ガスセンサ