Mg14Gd O-0.5Zr合金の硬さと引張降伏応力に及ぼす析出物の粒径,集合組織および密度の影響【Powered by NICT】

Effect of grain size, texture and density of precipitates on the hardness and tensile yield stress of Mg-14Gd-0.5Zr alloys

著者 (7件)： Li Rongguang (School of Mechanical Engineering, Shenyang University of Chemical Technology, Shenyang, China) ,  Xin Renlong (College of Materials Science and Engineering, Chongqing University, Chongqing, China) ,  Liu Qing (College of Materials Science and Engineering, Chongqing University, Chongqing, China) ,  Chapuis Adrien (College of Materials Science and Engineering, Chongqing University, Chongqing, China) ,  Liu Shifeng (College of Materials Science and Engineering, Chongqing University, Chongqing, China) ,  Fu Guangyan (School of Mechanical Engineering, Shenyang University of Chemical Technology, Shenyang, China) ,  Zong Lin (School of Mechanical Engineering, Shenyang University of Chemical Technology, Shenyang, China)
資料名： Materials & Design  (Materials & Design)
巻： 114  ページ： 450-458  発行年： 2017年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,時効硬化性Mg14Gd10-0.5Zr(wt.%)合金は,粒径,硬さに及ぼす析出物の組織と密度と0.2%耐力引張降伏応力の影響を調べるためのモデル材料として使用した。六種類の異なる結晶粒サイズ,集合組織と析出物の密度の試料を押出プロセスと時効処理を変えて調製した。試料のミクロ組織と集合組織を電子後方散乱回折と透過型電子顕微鏡で調べた。検討の結果,Mg-Gd合金の0.2%耐力降伏応力は結晶粒径と集合組織の影響を大きく受けたが,合金の硬さは主に析出物の密度によって制御されることを示した。本研究では,粒径,集合組織と析出物の密度は,Mg-Gd合金の硬さと0.2%耐力降伏応力に異なる影響を持つことができることを明らかにした。時効硬化性マグネシウム合金の機械的試験標準と完成ガイドラインに関する重要な問題を提起する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 透過型電子顕微鏡 ,  *析出物 ,  降伏強さ ,  *硬度 ,  マグネシウム合金 ,  *粒径 ,  結晶粒径 ,  *引張 ,  機械的検査 ,  *集合組織 ,  *降伏応力 ,  時効硬化 ,  *合金
準シソーラス用語： EBSD , 【Automatic Indexing@JST】

著者キーワード (6件)： 展伸マグネシウム合金 ,  耐力 ,  Hardness ,  粒径 ,  テクスチャ ,  析出硬化

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： 引張 ,  降伏応力 ,  析出物 ,  粒径 ,  集合組織 ,  密度