純ZrとZr基合金におけるδ′-ZrOの熱的に誘起された形成のその場透過電子顕微鏡観察【Powered by NICT】

In situ transmission electron microscopy study of the thermally induced formation of δ′-ZrO in pure Zr and Zr-based alloy

著者 (5件)： Yu Hongbing (Department of Mechanical and Materials Engineering, Queen’s University, 60 Union Street, Kingston, ON, CanadaK7L 3N6) ,  Yao Zhongwen (Department of Mechanical and Materials Engineering, Queen’s University, 60 Union Street, Kingston, ON, CanadaK7L 3N6) ,  Long Fei (Department of Mechanical and Materials Engineering, Queen’s University, 60 Union Street, Kingston, ON, CanadaK7L 3N6) ,  Saidi Peyman (Department of Mechanical and Materials Engineering, Queen’s University, 60 Union Street, Kingston, ON, CanadaK7L 3N6) ,  Daymond Mark R. (Department of Mechanical and Materials Engineering, Queen’s University, 60 Union Street, Kingston, ON, CanadaK7L 3N6)
資料名： Journal of Applied Crystallography  (Journal of Applied Crystallography)
巻： 50  号： 4  ページ： 1028-1035  発行年： 2017年 
JST資料番号： D0631A  ISSN： 0021-8898  CODEN： JACGAR  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： δ′-ZrO相の形成,透過型電子顕微鏡における973Kでの純ZrとZr Sn Nb Mo合金の透過型電子顕微鏡(TEM)薄膜のアニーリング過程での発生のその場観察を報告した。δ′-ZrOの格子パラメータを測定し,決定したωZr相のそれに類似していた。δ′-ZrO及びα-Zr相の間の方位関係はとして及び/又はとTEM薄箔標準に比較して,α結晶粒の方位に依存して同定されている。δ′-ZrOの核形成と成長を動的に観察した。本研究では,Zr合金の酸化機構を研究するための新しい便利な方法を示唆し,新しく報告されたδ’-ZrOの特性のより深い理解を提供する。δ′-ZrOであるωZrのそれと同一Zr副格子を持つので,αとδ′-ZrO相間の方位関係は,α-及びωZr間に存在する方位関係に光を当てる可能性があり,したがって,α-およびω-Ti。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 薄膜 ,  *ジルコニウム ,  *ジルコニウム合金 ,  副格子 ,  焼なまし ,  結晶粒 ,  *透過型電子顕微鏡 ,  その場観察 ,  核形成 ,  合金 ,  格子定数
準シソーラス用語： 透過型電子顕微鏡法 ,  酸化機構 , 【Automatic Indexing@JST】

著者キーワード (4件)： ZrO相 ,  その場加熱 ,  透過型電子顕微鏡観察 ,  TEM