0.9474BaTiO_3 0.0526Ba_2LiTa_5O_15に基づく非還元性高温安定誘電体の誘電特性と微細構造【Powered by NICT】

Dielectric properties and microstructures of non-reducible high-temperature stable dielectrics based on 0.9474BaTiO₃-0.0526Ba₂LiTa₅O₁₅

著者 (5件)： Li Jian-Hua (Dept. of Materials and Mineral Resources Engineering, National Taipei University of Technology, Taipei 106, Taiwan) ,  Li Jian-Hua (Holy Stone Enterprise Co. Ltd., Taipei, Taiwan) ,  Liu Yi-Xin (Dept. of Materials and Mineral Resources Engineering, National Taipei University of Technology, Taipei 106, Taiwan) ,  Wang Sea-Fue (Dept. of Materials and Mineral Resources Engineering, National Taipei University of Technology, Taipei 106, Taiwan) ,  Hung Yen-Po (Dept. of Materials and Mineral Resources Engineering, National Taipei University of Technology, Taipei 106, Taiwan)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： S1  ページ： S79-S84  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,Li_2TiO_3,MnCO_3,CaCO_3とSiO_2を含む種々のドーパントを含む0.95BaTiO_3 0~0.05Ba_2LiTa_5O_15化合物に基づく非還元性高温安定誘電体を固相反応により調製した。得られた最適組成は0.95BaTiO_3 0~0.05Ba_2LiTa_5O_15た5mo1%Li_2TiO_3,1.5mo1%MnCO_3,2.0mo1%CaCO_3と1.0mo1%SiO_2を添加した。3%H_2 97%N_2 3%H_2で2時間1070°Cで焼結し,100ppm O_2を含む雰囲気中で950°Cで熱処理した6時間後,tanδ:1.4%( 55°C)と11.2%(200°C),電気抵抗:200°Cで25°Cと7.5×10~9Ω-cmで1.2×10~11Ω-cm,及び誘電定数800 25°Cで,温度係数キャパシタンス(TCC)を含む誘電特性:200°Cで 55°Cと9.2% 3.6%が得られ,これはEIA仕様のX9R要求に合致する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *高温 ,  固相反応 ,  温度係数 ,  *誘電性 ,  焼結 ,  *誘電体 ,  静電容量 ,  *微細構造 ,  損失正接 ,  *還元性 ,  ドーパント ,  誘電率

著者キーワード (4件)： 温度安定誘電体 ,  X9R ,  MLCC ,  Microstructure

分類 (2件)： 強誘電体,反強誘電体,強弾性  (BM05030B) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： 還元性 ,  誘電体 ,  誘電特性 ,  微細構造