中間層としてSiCを用いた超硬合金基板上に蒸着したダイヤモンド皮膜調製と侵食抵抗試験【Powered by NICT】

Diamond coatings deposited on cemented carbide substrates with SiC as interlayers: Preparation and erosion resistance tests

著者 (6件)： Wang G. (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Lu X. (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Ding M. (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Liu Y. (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Tang W. (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhang B. (Baihui Xingye (Beijing) Technology Co. Ltd, Beijing 100142, China)
資料名： Diamond and Related Materials  (Diamond and Related Materials)
巻： 73  ページ： 105-113  発行年： 2017年 
JST資料番号： W0498A  ISSN： 0925-9635  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ダイヤモンド膜は様々な応用に有用な保護皮膜として使用できた。しかし超硬合金材料に,不適切な接着が問題にされていない。本研究では,ダイヤモンド被覆は,高電流アークプラズマ化学蒸着法による超硬合金基板上に作製した。良好な接着性を保証するために,SiCを中間層として基板上に堆積した。走査電子顕微鏡,エネルギー分散X線分光法,X線回折を用いて,中間層を特性化し,Raman分光法,引かき,押込み及びマイクロスラリージェットエロージョン試験はダイヤモンド被覆した試料の品質,接着性および耐エロージョン性を評価した。結果は,中間層としてSiCを用いたダイヤモンド被覆と基板間の良好な接着を確保する上で有効であることを実証した。結果として,ダイヤモンド被覆超硬合金の耐エロージョン性は一桁以上改善できる,未被覆超硬合金試料のそれと比較した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 化学蒸着 ,  *ダイヤモンド ,  接着 ,  エネルギー分散X線分光分析 ,  保護膜 ,  *皮膜 ,  *炭化ケイ素 ,  *超硬合金 ,  被覆 ,  走査電子顕微鏡 ,  Raman分光法 ,  エロージョン ,  ダイヤモンド被覆 ,  ダイヤモンド膜 ,  *中間層 ,  *鉱石 ,  *宝石

著者キーワード (5件)： ダイヤモンド被覆 ,  超硬 ,  SiC中間層 ,  接着 ,  耐エロージョン性

分類 (1件)： 炭素とその化合物  (YB02060D)

タイトルに関連する用語 (8件)： 中間層 ,  SiC ,  硬合金 ,  蒸着 ,  ダイヤモンド ,  皮膜 ,  調製 ,  侵食