ポリ乳酸グラフト化シランカップリング剤の調製とポリ乳酸/木粉複合材料への影響【JST・京大機械翻訳】

Preparation of Poly(Lactic Acid)Grafted with Silane Coupling Agent and Its Influence on Poly(Lactic Acid)/Wood Flour Composites

著者 (2件)： Yang Linqiang (Institute of Chemical Industry of Forestry Products,China Academy of Forestry(CAF),National Engineering Laboratory for Biomass Chemical Utilization,Key and Laboratory on Forest Chemical Engineering,State Forestry Administration (SFA),Key Laboratory of Biomass Energy and Material) ,  Jin Liwei (Institute of Chemical Industry of Forestry Products,China Academy of Forestry(CAF),National Engineering Laboratory for Biomass Chemical Utilization,Key and Laboratory on Forest Chemical Engineering,State Forestry Administration (SFA),Key Laboratory of Biomass Energy and Material)
資料名： Gaofenzi Cailiao Kexue yu Gongcheng  (Gaofenzi Cailiao Kexue yu Gongcheng)
巻： 32  号： 7  ページ： 125-130  発行年： 2016年 
JST資料番号： C2119A  ISSN： 1000-7555  CODEN： GCKGEI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： Γ-(メチル)イソプロピルアクリルアミド(PLA-G-MPS)を,反応押出によって調製し,そして,ポリ乳酸/木粉(PLA/PLA)複合材料におけるそれらのカップリング効果を研究した。1H-NMRスペクトルは,MPSがPLA上にグラフト化されることを示した。溶媒相溶化複合材料粒子中のPLA相を用いてWF相を得て,その赤外スペクトルの解析から,PLA-G-MPSがWFと共有結合することが分かった。機械的性質試験により,高分子量カップリング剤の添加量が3%のとき,引張強さ,曲げ強さおよび衝撃強さは,それぞれ,17.5%,12.4%および88.4%増加した。複合材料の動的機械分析は,高分子カップリング剤の添加がPLAとWF間の相互作用力を向上させ,ガラス状態での材料の貯蔵弾性率を増加させることを示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 曲げ強さ ,  *シランカップリング剤 ,  高分子量 ,  カップリング効果 ,  赤外スペクトル ,  *木粉 ,  *カップリング剤 ,  陽子磁気共鳴 ,  動的機械分析 ,  共有結合 ,  *複合材料 ,  動弾性係数 ,  引張強さ ,  *移植片
準シソーラス用語： 反応押出 , 【Automatic Indexing@JST】

著者キーワード (4件)： poly(lactic acid) ,  γ-methacryloxy propyl trimethoxyl silane ,  reactive extrusion ,  coupling effect

分類 (2件)： 充填剤,補強材  (YH05030J) ,  機械的性質  (YH02022L)

タイトルに関連する用語 (6件)： ポリ乳酸 ,  グラフト ,  シランカップリング剤 ,  調製 ,  木粉 ,  複合材料