エチレン酢酸ビニルブロックの乾燥滑り摩擦:多孔性の影響【Powered by NICT】

Dry sliding friction of ethylene vinyl acetate blocks: Effect of the porosity

著者 (8件)： Yamaguchi Takeshi (Graduate School of Engineering, Tohoku University, Sendai, Miyagi, Japan) ,  Yamaguchi Takeshi (Graduate School of Biomedical Engineering, Tohoku University, Sendai, Miyagi, Japan) ,  Sugawara Takehiko (Graduate School of Engineering, Tohoku University, Sendai, Miyagi, Japan) ,  Takahashi Motoi (Graduate School of Engineering, Tohoku University, Sendai, Miyagi, Japan) ,  Shibata Kei (Graduate School of Engineering, Tohoku University, Sendai, Miyagi, Japan) ,  Moriyasu Kenta (Institute of Sports Science, ASICS Corporation, Kobe, Japan) ,  Nishiwaki Tsuyoshi (Institute of Sports Science, ASICS Corporation, Kobe, Japan) ,  Hokkirigawa Kazuo (Graduate School of Engineering, Tohoku University, Sendai, Miyagi, Japan)
資料名： Tribology International  (Tribology International)
巻： 116  ページ： 264-271  発行年： 2017年 
JST資料番号： E0409B  ISSN： 0301-679X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,空隙率(α)値を変えたエチレン酢酸ビニル(EVA)ブロックの乾燥滑り摩擦特性を調べるために最初の試みである。滑り摩擦試験は,多孔性が摩擦係数(すなわち,摩擦係数αとき,α<50%で減少し,αとα>50%増加)に有意に影響することを示した。より高い間隙率(α>80%)を有するEVAブロックは非多孔性EVAブロックより大きな摩擦係数を示した。ガラス板上の接触面積の観察は,大きな多孔度を有する多孔性EVAブロックの前部での弾性崩壊を明らかにした。細胞壁の弾性座屈による多孔性EVAブロックの弾性崩壊を考慮した単純化したモデルは接着摩擦の摩擦係数に及ぼす多孔性の影響を説明した。,より高いαは見かけの接触面積の前部での弾性崩壊面積の増加の結果としてより大きな接触面積を提供し,高い摩擦係数をもたらした。これらの結果は,高摩擦材料としての多孔質重合体の新規用途への洞察を提供する可能性がある。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *多孔性 ,  簡素化 ,  *滑り摩擦 ,  弾性 ,  モデル ,  摩擦係数 ,  空隙率 ,  接着 ,  板ガラス ,  摩擦材料 ,  脂肪酸 ,  脂肪族アルコール ,  エノールエステル ,  ビニル化合物 ,  不飽和アルコール ,  アルケン
準シソーラス用語： 接触面積 ,  摩擦特性 ,  *乾燥滑り , 【Automatic Indexing@JST】

著者キーワード (4件)： 滑り ,  乾燥 ,  多孔質 ,  高分子

分類 (1件)： 潤滑一般  (QB02010S)

物質索引 (2件)： 酢酸ビニル ,  エチレン

タイトルに関連する用語 (3件)： エチレン酢酸ビニル ,  滑り摩擦 ,  多孔性