Al_2O_3 SiO_2~-K2O Na_2Oシステムを用いた高強度アルミナ磁器絶縁体上のその場高温X線回折研究【Powered by NICT】

In situ high temperature X-ray diffraction study on high strength aluminous porcelain insulator with the Al₂O₃-SiO₂-K2O-Na₂O system

著者 (6件)： Meng Yong (State Key Laboratory of Ore Deposit Geochemistry, Institute of Geochemistry, Chinese Academy of Sciences, Guiyang 550002, Guizhou, China) ,  Meng Yong (University of Chinese Academy of Sciences, Beijing 100049, China) ,  Gong Guohong (State Key Laboratory of Ore Deposit Geochemistry, Institute of Geochemistry, Chinese Academy of Sciences, Guiyang 550002, Guizhou, China) ,  Wei Dongtian (State Key Laboratory of Ore Deposit Geochemistry, Institute of Geochemistry, Chinese Academy of Sciences, Guiyang 550002, Guizhou, China) ,  Wei Dongtian (University of Chinese Academy of Sciences, Beijing 100049, China) ,  Xie Yumin (Bijie Highland Porcelain Insulator Limited Liability Company, Bijie 551700, Guizhou, China)
資料名： Applied Clay Science  (Applied Clay Science)
巻： 132-133  ページ： 760-767  発行年： 2016年 
JST資料番号： B0687B  ISSN： 0169-1317  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： カオリナイト,コランダム,微斜長石,石英,少量曹長石とアナターゼの鉱物組成を用いた高強度アルミナ磁器絶縁体は25°Cから1300°Cにおけるその場高温XRD(HTXRD)によって調べた。磁器絶縁体に含まれる鉱物の量変化と反応を鮮やかに提示した。全プロセスを連続段階で起こった:1)カオリナイト非晶質メタカオリナイトへ分解500 600°Cの温度範囲2)反応生成物を約1000°Cまで非晶質形を保った。3)約1000°Cで,非晶質反応生成物を一次ムライトを生成した;4)回1200°C後,微斜長石が融解し始め,二次ムライトへの一次ムライトの成長を促進するアルカリ性液相を形成する;5)アルカリ液相はβ-石英をエッチングし,β-石英減少の反射強度をもたらした;6)コランダムは全加熱過程で非常に安定であった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 石英 ,  *絶縁材料 ,  鉱物組成 ,  カオリナイト ,  非晶質 ,  ムライト ,  *X線回折 ,  コランダム ,  曹長石 ,  *高温 ,  液相 ,  *磁器 ,  斜長石 ,  *アルミナ磁器 ,  アナターゼ ,  *絶縁体 ,  相

著者キーワード (5件)： その場高温 ,  XRD ,  磁器絶縁体 ,  鉱物 ,  反応

分類 (3件)： 珪酸塩鉱物  (DE08030A) ,  セラミック・陶磁器の製造  (YC03020V) ,  セラミック・陶磁器一般  (YC03010K)

タイトルに関連する用語 (6件)： K2O ,  高強度 ,  アルミナ磁器 ,  絶縁体 ,  X線回折 ,  研究