高電流パルス電子ビームにより誘起された表面合金化処理後のM50鋼に及ぼすTa合金層の微細構造【Powered by NICT】

The microstructure of Ta alloying layer on M50 steel after surface alloying treatment induced by high current pulsed electron beam

著者 (7件)： Luo Dian (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, China) ,  Tang Guangze (School of Material Science & Engineering, Harbin Institute of Technology, Harbin, 150001, China) ,  Ma Xinxin (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, China) ,  Gu Le (School of Mechatronics Engineering, Harbin Institute of Technology, Harbin, 150001, China) ,  Wang Liqin (School of Mechatronics Engineering, Harbin Institute of Technology, Harbin, 150001, China) ,  Wu Tingbao (Harbin Bearing Company of CNAC Group, Harbin, 150001, China) ,  Ma Fang (Harbin Bearing Company of CNAC Group, Harbin, 150001, China)
資料名： Vacuum  (Vacuum)
巻： 136  ページ： 121-128  発行年： 2017年 
JST資料番号： E0347A  ISSN： 0042-207X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,タンタルは,高電流パルス電子ビームによる表面合金化処理後のミクロ組織を調べるためにM50鋼の表面層に合金元素であることを選択した。Ta膜の異なる厚さは照射前のDCマグネトロンスパッタリングによるM50鋼上に蒸着し,表面合金化処理後の表面と断面の形態が観察された。合金化層の微細構造をX線回折と透過型電子顕微鏡で調べた。結果は合金層は三層に分割できることを明らかにした。トップ層は合金元素特にTaの偏析に起因する樹状突起と小中空球状構造を持つδ-Fe相から成っていた。いくつかの大きな球状と少数の樹枝状微細構造は,第二層で観察された;が合金化層の底部でラスマルテンサイトミクロ組織のみであった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *タンタル合金 ,  合金元素 ,  透過型電子顕微鏡 ,  *微細構造 ,  偏析 ,  タンタル ,  *合金層 ,  *鋼 ,  表層 ,  X線回折
準シソーラス用語： ラスマルテンサイト ,  中空球 ,  DCマグネトロンスパッタリング ,  *表面合金化 ,  *パルス電子ビーム , 【Automatic Indexing@JST】

著者キーワード (3件)： 高電流パルス電子ビーム ,  表面合金化 ,  δ-Fe相

分類 (2件)： その他の表面処理  (WC08070F) ,  金属の機械的性質  (BL01022T)

タイトルに関連する用語 (6件)： 高電流 ,  パルス電子ビーム ,  誘起 ,  表面合金化 ,  Ta合金 ,  微細構造