高Nb TiAl合金を含むにおけるB2→ω関連相転移の原子スケール観察【Powered by NICT】

Atomic-scale observations of B2→ω-related phases transition in high-Nb containing TiAl alloy

著者 (6件)： Wang Xuyang (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, China) ,  Yang Jieren (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, China) ,  Zhang Keren (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, China) ,  Hu Rui (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, China) ,  Song Lin (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, China) ,  Fu Hengzhi (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, China)
資料名： Materials Characterization  (Materials Characterization)
巻： 130  ページ： 135-138  発行年： 2017年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： Ti-45Al-8.5Nb-(W, B, Y)(at.%)合金におけるB2相領域内のω関連相の核形成を,透過型電子顕微鏡(TEM)および高分解能電子顕微鏡(H REM)により調べた。850°Cで,準安定B2相はω粒子に分解する。高分解能画像からの実験的証拠は,第一原子はB2構造の再分布と,元の11~1B2面はB2→ω」,「拡散崩壊」経路を表す中の崩壊することを明らかにした。ω′′→ω_o,[0001]ω領域における(0001)ω面のさらなる崩壊を逐次及び不均一プロセスよりもむしろ瞬間遷移,不均一構造遷移はエネルギー障壁を減少させることができることに起因している可能性がある。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *相転移 ,  透過型電子顕微鏡 ,  *合金 ,  核形成 ,  再分布
準シソーラス用語： エネルギー障壁 ,  B2相 ,  *原子スケール ,  *チタンアルミニウム合金 , 【Automatic Indexing@JST】

著者キーワード (5件)： TiAl合金 ,  透過型電子顕微鏡(TEM) ,  拡散 ,  相変態 ,  オメガ相

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： Nb ,  TiAl合金 ,  相転移 ,  原子スケール ,  観察