常圧焼結中のGd_2Zr_2O_7ナノセラミックのち密化と粒成長【Powered by NICT】

Densification and grain growth of Gd₂Zr₂O₇ nanoceramics during pressureless sintering

著者 (18件)： Zhou Mao (College of Physical Science and Technology, Sichuan University, Chengdu 610064, China) ,  Zhou Mao (Key Laboratory of Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Huang Zhangyi (College of Physical Science and Technology, Sichuan University, Chengdu 610064, China) ,  Huang Zhangyi (Key Laboratory of Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Qi Jianqi (College of Physical Science and Technology, Sichuan University, Chengdu 610064, China) ,  Qi Jianqi (Key Laboratory of Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Wei Nian (College of Physical Science and Technology, Sichuan University, Chengdu 610064, China) ,  Wei Nian (Key Laboratory of High Energy Density Physics of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Wu Di (The Gene and Linda Voiland School of Chemical Engineering and Bioengineering, Washington State University, Pullman, WA 99163, United States) ,  Zhang Qinghua (College of Physical Science and Technology, Sichuan University, Chengdu 610064, China) ,  Zhang Qinghua (Key Laboratory of Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Wang Shanshan (College of Physical Science and Technology, Sichuan University, Chengdu 610064, China) ,  Wang Shanshan (Key Laboratory of Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Feng Zhao (College of Physical Science and Technology, Sichuan University, Chengdu 610064, China) ,  Feng Zhao (Key Laboratory of Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Lu Tiecheng (College of Physical Science and Technology, Sichuan University, Chengdu 610064, China) ,  Lu Tiecheng (Key Laboratory of Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Lu Tiecheng (Key Laboratory of High Energy Density Physics of Ministry of Education, Sichuan University, Chengdu 610064, China)
資料名： Journal of the European Ceramic Society  (Journal of the European Ceramic Society)
巻： 37  号： 3  ページ： 1059-1065  発行年： 2017年 
JST資料番号： E0801B  ISSN： 0955-2219  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Gd_2Zr_2O_7ナノセラミックを常圧焼結法を用いて作製した,ナノ粉末をソルボサーマル法により合成した。セラミックの焼結中の粒成長と緻密化に及ぼす出発粉末の効果を明らかにした。調べ,通常および二段階焼結した二つの異なる常圧焼結法。焼結温度は,従来の焼結中の増加すると試料の粒径は急激に増大する。対照的に,二段階焼結における,異常または不連続結晶粒成長は第二段階で抑制され,Gd_2Zr_2O_7ナノセラミック形成(平均粒径83nm,相対密度~93%)をもたらした。このような異なる挙動は,粒界移動と拡散のような動力学的因子の間の相互作用に起因すると考えられる。,粒成長の抑制と二段階焼結におけるち密化の促進は,主に第二段階焼結プロセス中の結晶粒界拡散の支配的役割に起因した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 粒界拡散 ,  *結晶成長 ,  相対密度 ,  *焼結 ,  粒径 ,  粒界移動 ,  *緻密化 ,  *セラミック ,  *常圧 ,  焼結温度 ,  二段階焼結 ,  ソルボサーマル合成 ,  ナノ粉末 ,  *ナノセラミック ,  *常圧焼結

著者キーワード (4件)： Gd_2Zr_2O_7ナノセラミック ,  常圧焼法 ,  ち密化挙動 ,  2段階焼結

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (4件)： 常圧焼結 ,  セラミック ,  ち密化 ,  粒成長