Cu_0 0.05Bi_2Te_3の微細構造と熱電特性に及ぼすSeドーピングおよび/またはBi添加の影響【Powered by NICT】

Influence of Se-doping and/or Bi addition on microstructure and thermoelectric properties of Cu_0.05Bi₂Te₃

著者 (4件)： Chen Song (Key Laboratory of Advanced Civil Engineering Materials of Ministry of Education, School of Materials Science & Engineering, Tongji University, 4800 Caoan Road, Shanghai 201804, China) ,  Chen Song (School of Materials Science and Engineering, Fujian University of Technology, Fuzhou 350108, China) ,  Cai Kefeng (Key Laboratory of Advanced Civil Engineering Materials of Ministry of Education, School of Materials Science & Engineering, Tongji University, 4800 Caoan Road, Shanghai 201804, China) ,  Shen Shirley (CSIRO Manufacturing, Gate 3, Normanby Road, Clayton, VIC 3190, Australia)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 1 PA  ページ： 599-603  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Cu_0 0.05Bi_2Se_xTe_3x(x=0.2,0.3,0.4)バルク試料をガス誘起還元法により合成しホットプレス対応するナノ粉末により作製した。Seドーピングはキャリア濃度,試料の電気伝導率を有意に増加させた。これに基づいて,より高い力率をもつCu_0 0.05Bi_2Se_0 3Te_2 7サンプルは,元のサンプルとして選択した;Cu_0 0.05Bi_2Se_0 3Te_2 7ナノ粉末を種々の量のBiナノ粒子(NPs)を混合し,バルク試料にホットプレスした。Bi NPsの添加は試料の焼結を促進した。添加されたBi NPsの含有量が低いとき(≦1wt%),電気伝導率は,純粋な試料よりも高く,全てのBi NP添加試料は,元の試料よりも高いSeebeck係数を持ち,従って,パワーファクタが改善された。最大力率,30.6μWcm~ 1K~ 2は2wt%Bi NPs添加試料で得られた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ナノ構造 ,  ナノ粒子 ,  *セレン ,  キャリア密度 ,  焼結 ,  *ビスマス ,  電気伝導率 ,  微細構造 ,  ホットプレス ,  力率
準シソーラス用語： Seebeck係数 ,  ナノ粉末 ,  *熱電特性 , 【Automatic Indexing@JST】

著者キーワード (4件)： Bi_2Te_3 ,  熱電 ,  ドーピング ,  ナノ構造

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (5件)： 微細構造 ,  熱電特性 ,  Se ,  ドーピング ,  Bi