リチウムチタン酸化物を用いたLiNi_0 5Co_0 2Mn_0 3O_2陰極材料の高カットオフ電圧サイクル安定性を強化するための容易な方法【Powered by NICT】

A facile approach to enhance high-cutoff voltage cycle stability of LiNi_0.5Co_0.2Mn_0.3O₂ cathode materials using lithium titanium oxide

著者 (6件)： Zhang Manfang (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Hu Guorong (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Wu Lili (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Peng Zhongdong (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Du Ke (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Cao Yanbing (School of Metallurgy and Environment, Central South University, Changsha 410083, China)
資料名： Electrochimica Acta  (Electrochimica Acta)
巻： 232  ページ： 80-88  発行年： 2017年 
JST資料番号： B0535B  ISSN： 0013-4686  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： リチウムイオン電池のためのリチウムチタン酸化物で被覆したNiベース層状LiNi_0 5Co_0 2Mn_0 3O_2(NCM)化合物はTiO_2粉末とCH_3COOLiを用いた簡単な固相合成プロセスにより達成することに成功した。構造,形態および電気化学的性質の系統的測定を適用した。X線回折パターンは,リチウムチタン酸化物(Li_4Ti_5O_12とLi_7Ti_5O_12がLTOとして標識される)の存在と転化率を示した。LTOの形で被覆層が観察され,厚さは均一に分布した約10nmであった。同様に,XPSは,LTOの存在を確認した。1.0wt.%LTO被覆NCM材料は4.5Vのカットオフ電圧で100サイクル後の裸の(64.3%)のそれよりも91.0%の高い容量保持を示した。一方,LTO被覆NCM材料は,60°Cで無添加試料と比較して有意に改善された熱安定性を示した。添加では,LTO修飾による電極の電気化学的性能を向上させることが有効であることを証明した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 被覆 ,  リチウムイオン電池 ,  X線回折 ,  *リチウム ,  熱安定性 ,  粉体 ,  転化率 ,  *酸化チタン ,  固相合成 ,  被覆層 ,  *臨界電圧
準シソーラス用語： 電気化学的性能 ,  電気化学的特性 , 【Automatic Indexing@JST】

著者キーワード (5件)： LiNi_0 5Co_0 2Mn_0 3O_2 ,  リチウムチタン酸化物 ,  サイクル性能 ,  高カットオフ電圧 ,  高温

分類 (2件)： 二次電池  (YB04030K) ,  電気化学反応  (CB07050F)

タイトルに関連する用語 (6件)： リチウム ,  チタン酸化物 ,  陰極材料 ,  カットオフ電圧 ,  サイクル安定性 ,  強化