残留剛性モデルを用いた複合材料スリーブの疲労寿命評価【Powered by NICT】

Fatigue life evaluation of composite material sleeve using a residual stiffness model

著者 (6件)： Kim Jong-Sung (Sejong University, Department of Nuclear Engineering, 209 Neungdong-ro, Gwangjin-gu, Seoul 05006, Republic of Korea) ,  Bae Kyung-Dong (Korea University, Department of Mechanical Engineering, Anam-Dong, Seongbuk-Ku, Seoul 02841, Republic of Korea) ,  Lee Chul (Sejong University, Department of Nuclear Engineering, 209 Neungdong-ro, Gwangjin-gu, Seoul 05006, Republic of Korea) ,  Kim Yun-Jae (Korea University, Department of Mechanical Engineering, Anam-Dong, Seongbuk-Ku, Seoul 02841, Republic of Korea) ,  Kim Woo-Sik (Gas Facility Technology Center, KOGAS Research Institute, Il-Dong, Sangnok-Ku, Ansan 426-860, Republic of Korea) ,  Kim Ik-Joong (Gas Facility Technology Center, KOGAS Research Institute, Il-Dong, Sangnok-Ku, Ansan 426-860, Republic of Korea)
資料名： International Journal of Fatigue  (International Journal of Fatigue)
巻： 101  号： P1  ページ： 86-95  発行年： 2017年 
JST資料番号： D0802B  ISSN： 0142-1123  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,疲れ評価は複合材料スリーブを用いて修復埋設天然ガスパイプの疲労寿命を評価するために行った。重ねせん断引張と剪断疲れ試験を行い,最初に機械的性質を決定し,損傷モデルを確立するために行った。試験結果から,複合材料スリーブの損傷モデルを決定し,接着損傷に起因する剛性低下現象に基づいた。有限要素損傷解析によるASMEB&PVコードSecで提示した損傷モデルと構造応力/破壊力学手法を用いた。VIII Div.剥離の発生後の損傷パイプの2剥離挙動,損傷管の破裂圧力と疲労寿命を調べた。その結果,パイプの腐食損傷周辺で発生した接着剤ダメージによる複合層の間の剥離も接着剤の損傷は埋設天然ガスパイプの疲れ寿命に大きく影響しないことを確認した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *疲れ寿命 ,  *剛性 ,  埋設 ,  剪断 ,  *複合材料 ,  接着剤 ,  接着 ,  天然ガス ,  破壊力学 ,  疲れ試験 ,  *スリーブ ,  引張
準シソーラス用語： 腐食損傷 ,  損傷解析 ,  損傷モデル , 【Automatic Indexing@JST】

著者キーワード (5件)： 疲労寿命評価 ,  複合材料スリーブ ,  埋設天然ガスパイプ ,  残留剛性モデル ,  有限要素損傷解析