水溶液からポリ(3,4-エチレンジオキシチオフェン)と還元グラフェン酸化物による交互に積層した多層膜の電解合成【Powered by NICT】

Electrosynthesis of a multilayer film stacked alternately by poly(3,4-ethylenedioxythiophene) and reduced graphene oxide from aqueous solution

著者 (4件)： Imae Ichiro (Department of Applied Chemistry, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8527, Japan) ,  Fujimoto Daiki (Department of Applied Chemistry, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8527, Japan) ,  Zhang Lu (Department of Applied Chemistry, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8527, Japan) ,  Harima Yutaka (Department of Applied Chemistry, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8527, Japan)
資料名： Electrochemistry Communications  (Electrochemistry Communications)
巻： 81  ページ： 65-69  発行年： 2017年 
JST資料番号： W1133A  ISSN： 1388-2481  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ポリ(3,4-エチレンジオキシチオフェン)と還元グラフェン酸化物で交互に積層した多層膜は,EDOT繰返し酸化により3,4-エチレンジオキシチオフェン(EDOT)と酸化グラフェン(GO)を含む単一水溶液から電気化学的に合成し,導電性基板上にGOを低減した。提案した技術を用いて,異なる層の厚さは電解時間を変化させることによって容易に調整することができ,層の数は電位ステップの配列を繰り返すことによって簡単に増加できた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *還元 ,  電位 ,  電気化学 ,  *水溶液 ,  *グラフェン ,  *多層膜 ,  導電性 ,  *ポリエチレンジオキシチオフェン ,  *多層 ,  *電解合成 ,  *電解
準シソーラス用語： 繰返し酸化 ,  *酸化グラフェン , 【Automatic Indexing@JST】

著者キーワード (5件)： ポリ(34-エチレンジオキシチオフェン) ,  グラフェン ,  電解合成 ,  多層 ,  複合材料

分類 (2件)： 高分子固体の物理的性質  (CG02024U) ,  電気化学反応  (CB07050F)

タイトルに関連する用語 (4件)： 水溶液 ,  還元グラフェン酸化物 ,  多層膜 ,  電解合成